通过将不同摩尔配比的丙二酸乙二醇酯嵌入到芳香族水溶性聚酯的分子主链中,制备出一系列具有不同分子结构的环保型脂肪族-芳香族水溶性共聚酯(WSACP)。然后,以WSACP溶液在聚酯纤维上的接触角、WSACP膜的拉伸力学性能以及WSACP对聚酯纤维的粘合强度为主要量化指标,研究了脂肪族单体丙二酸二甲酯(DMM)与芳香族单体对苯二甲酸二甲酯(DMT)的单体配伍对WSACP与聚酯纤维粘合性能的影响。结果表明:当DMM:DMT=3:7(摩尔比)时,合成的WSACP对聚酯纤维的粘合性能较为优异。
A series of water-soluble aliphatic-aromatic copolyesters (WSACP) with different molecular structures were prepared through incorporating various molar amount of ethylene malonate into the backbone of water-soluble aromatic polyester.In terms of contact angel of WSACP solution on polyester fibers,tensile properties of WSACP film,and adhesive strength to polyester fibers,effects of monomer compatibility of dimethyl malonate (DMM)/dimethyl terephthalate (DMT) on the adhesion of WSACP to polyester fibers were studied.The experimental results showed that the adhesion of WSACP to polyester fiber was better when the feed molar ratio of DMM/DMT was 3:7 (mole ratio).
[1] Jin E Q,Zhu Z F,Yang Y Q.Structural effects of glycol and benzenedicarboxylate units on the adhesion of water-soluble polyester sizes to polyester fibers[J].Journal of the Textile Institute,2010,101(12):1112-1120.
[2] 陈大俊,林庆辉.一种以铝化合物为催化剂制备水溶性聚酯的方法:中国,CN 102558527B[P].2013-11-13.
[3] 冷世伟,胡文.一种POSS改性的水溶性聚酯树脂及制备方法及含有该聚酯的水性涂料:中国,CN 103360586B[P].2015-08-26.
[4] 何曼君,陈维孝,董西侠.高分子物理[M].上海:复旦大学出版社,2003,174-182.
[5] Jin E Q,Zhu Z F,Zhang H.Film-formation investigation on polyester sizes for measuring the mechanical behaviors for warp sizing[J].Man-Made Textiles in India,2008,51(8):274-277.
[6] Jin E Q,Li M L,Xi B J,et al.Effects of molecular structure of acrylates on sizing performance of allyl grafted starch[J].Indian Journal of Fibre & Textile Research,2015,40(4):437-446.
[7] Deng L M,Wang Y Z,Yang K K,et al.A new biodegradable copolyester poly(butylene succinate-co-ethylene succinate-co-ethylene terephthalate)[J].Acta Materialia,2004,52(20):5871-5878.
[8] 陈玉英.药学实用仪器分析[M].北京:高等教育出版社,2006,270-271.
[9] Zhu Z F,Chen P H.Carbamoyl ethylation of starch for enhancing the adhesion capacity to fibers[J].Journal of Applied Polymer Science,2007,106(4):2763-2768.
[10] 许新建.生物可降解脂肪族/芳香族共聚酯(PBST)纤维的制备及其性能研究[D].上海:东华大学,2007.
基金资助
绍兴市公益性技术应用研究计划项目(2014B70014);浙江省教育厅科研计划项目(Y201533919);浙江省公益性技术应用研究计划项目(2016C34009);国家级大学生创新创业训练计划项目(201610349002)
PDF