热处理时间对锐钛矿TiO₂光催化性能的影响

^1,2

^1,2*

作者信息 +

Influence of heat treatment holding time on photocatalytic activity of anatase TiO₂

Zhu Xiaodong^1,2, Feng Wei^1,2, Fang Jiaqin¹, Xu Hong¹, Hou Zhongwen¹
Zhong Yu¹, Luo Jing³, Lu Yurong³

Author information +

文章历史 +

Received		Published
2017-03-18		2017-10-19
Issue Date	Revised Date
2017-10-19	2017-03-18

PDF

摘要

以钛酸丁酯为原料,冰醋酸为抑制剂,无水乙醇为溶剂,采用溶胶凝-胶法制备了TiO₂,对其进行了450℃不同保温时间的退火处理。利用XRD、SEM、EDS、XPS等测试技术对样品进行晶型、形貌、元素组成及价态的表征。结果表明,不同保温时间退火处理的TiO₂都生成了锐钛矿,随保温时间增加晶粒尺寸与晶型完整度增加;TiO₂颗粒呈现近似球形形貌。以亚甲基蓝为目标污染物,考察了样品的光催化效率,结果表明,保温1h的TiO₂具有最大的降解率与反应速率常数,光照3h后,其降解率达到80.9%,反应速率常数为0.562h^-1。

Abstract

TiO₂ particle was synthesized by sol-gel method using tetrabutyl titanate as raw material,glacial acetic acid as inhibitor,and absolute ethanol as solvent.The particle was annealed at 450℃ with different holding time.The crystal structure,morphology,element composition and the chemical state of samples were analyzed by XRD,SEM,EDS and XPS,respectively.The results showed that all the samples formed the anatase structure and TiO₂ particles presented approximate spherical morphology.The grain size and crystal structure integrity increased with increasing holding time.The methylene blue was used as the target pollutant to test the photocatalytic activity of sample.The results revealed that highest photocatalytic activity and reaction rate constant were obtained on TiO₂ which was annealing for 1 h.After light irradiation for 3h,the degradation rate and the reaction rate constant reached 80.9% and 0.562h^-1,respectively.

关键词

热处理 / 保温时间 / TiO₂ / 光催化性能

Key words

heat treatment / holding time / TiO₂ / photocatalytic activity

引用本文

引用格式 ▾

热处理时间对锐钛矿TiO₂光催化性能的影响[J]. 化工新型材料, 2017, 45(9): 181-183 DOI:

登录浏览全文

4963

注册一个新账户忘记密码

参考文献

原文顺序 | 出版日期 | 本文引用

[1] Li H,Hao Y B,Lu H Q,et al.A systematic study on visible-light N-doped TiO₂ photocatalyst obtained from ethylenediamine by sol-gel method[J].Applied Surface Science,2015,344:112-118.
[2] 张鹏会,李艳春,胡浩斌,等.B、N和Ce共掺杂TiO₂光催化降解染料废水研究[J].化工新型材料,2016,44(3):229-231.
[3] Lin H J,Yang T S,Hsi C S,et al.Optical and photocatalytic properties of Fe³⁺-doped TiO₂ thin films prepared by a sol-gel spin coating[J].Ceramics International,2014,40(7):10633-10640.
[4] Sun D F,Wang K,Xu Z J,et al.Synthesis and photocatalytic activity of sulfate modified Nd-doped TiO₂ under visible light irradiation[J].Journal of Rare Earths,2015,33(5):491-497.
[5] Zhao W Y,Bala H,Chen J K,et al.Thickness-dependent electron transport performance of mesoporous TiO₂ thin film for dye-sensitized solar cells[J].Electrochimica Acta,2013,114:318-324.
[6] Kalanur S S,Hwang Y J,Joo O S.Construction of efficient CdS-TiO₂ heterojunction for enhanced photocurrent,photostability,and photoelectron lifetimes[J].Journal of Colloid and Interface Science,2013,402(14):94-99.
[7] Wang H F,Tang B,Li X Y,et al.Antibacterial properties and corrosion resistance of nitrogen-doped TiO₂ coating on stainless steel[J].Journal of Materials Science and Technology,2011,27(4):309-316.
[8] 杨志广,王筠,吴亚楠,等.TiO₂纳米管的制备及其抑菌性能研究[J].化工新型材料,2015,43(7):60-62.
[9] 金冲,张卫国,姚素薇,等.热处理工艺对TiO₂纳米管阵列结构及其光电性能的影响[J].无机材料学报,2012,27(1):54-58.
[10] Li M T,He J L.Synthesis and room-temperature ferromagnetism of porous V-doped rutile TiO₂ microspheres[J].Materials Letters,2016,174:48-52.
[11] 刘蒙蒙,刘华,姜男哲,等.纳米TiO₂从无定型到锐钛矿型快速相变机理研究[J].化工新型材料,2015,43(5):164-166.
[12] Uvarov V,Popov I.Metrological characterization of X-ray diffraction methods for determination of crystallite size in nano-scale materials[J].Materials Characterization,2007,58(10):883-891.
[13] 代福,李宏业,李嘉琪,等.溶胶-凝胶法制备TiO₂薄膜光催化特性实验研究[J].材料导报,2014,28(8):40-43.
[14] Huang D G,Liao S J,Zhou W B,et al.Synthesis of samarium and nitrogen co-doped TiO₂ by modified hydrothermal method and its photocatalytic performance for the degradation of 4-chlorophenol[J].Journal of Physics and Chemistry of Solids,2009,70(5):853-859.
[15] Yamaki T,Umebayashi T,Sumita T,et al.Fluorine-doping in titanium dioxide by ion implantation technique[J].Nuclear Instruments and Methods in Physics Research B,2003,206:254-258.
[16] Ali I,Kim S R,Kim S P,et al.Anodization of bismuth doped TiO₂ nanotubes composite for photocatalytic degradation of phenol in visible light[J].Catalysis Today,2017,282:31-37.
[17] Nogawa T,Isobe T,Matsushita S,et al.Preparation and visible-light photocatalytic activity of Au-and Cu-modified TiO₂ powders[J].Materials Letters,2012,82:174-177.
[18] 张玉娟,沈嘉年.TiO₂光催化纳米薄膜的晶化处理[J].稀有金属材料与工程,2006,35(1):92-95.
[19] Shafaei A,Nikazar M,Arami M.Photocatalytic degradation of terephthalic acid using titania and zinc oxide photocatalysts:comparative study[J].Desalination,2010,252(1-3):8-16.