为使氯化丁基橡胶(CIIR)的阻尼温域向高温移动并具有一定的力学性能,填充炭黑(N330)和溴化对叔辛基苯酚甲醛树脂(HY-2055),制得CIIR阻尼材料。实验结果表明,材料的力学性能和阻尼性能与炭黑的品种和用量有明显的关系。填充酚醛树脂有效实现了阻尼温域向高温移动。当N330为40份(质量分数),HY-2055为50份(质量分数)时,制得的阻尼材料的拉伸强度为11.6MPa,扯断伸长率703%,直角撕裂强度25.4kN/m,300%定伸应力3.82MPa,压缩永久变形30%,损耗因子(tanδ)最大值0.875,损耗因子为0.4的阻尼温域为-27.9～37.4℃。
Abstract
Rubber damping materials were prepared by filling carbon black and brominated p-tert-octyl phenol formaldehyde resin in order to moving damping temperature range of CIIR to higher temperature and providing with good mechanical property.Experiment showed that the mechanical and damping properties of materials were obviously related to the variety and dosage of carbon black.And filling of phenolic resin moved damping temperature range to higher temperature effectively.When the mass fraction of carbon black N330 and HY-2055 were 40 and 50,the tensile strength of damping materials was 11.6MPa,elongation at break was 703%,rectangular tear strength was 25.4kN/m,300% of set pressure was 3.82MPa,the compression permanent deformation was 30%,the maximum of tanδ was 0.875,the damping temperature range was -27.9～37.4℃ when tanδ was 0.4.
关键词
氯化丁基橡胶
/
酚醛树脂
/
炭黑
/
力学性能
/
阻尼性能
Key words
CIIR
/
phenolic resin
/
carbon black
/
mechanical property
/
damping property
炭黑对氯化丁基橡胶阻尼材料性能影响研究[J].
化工新型材料, 2017, 45(9): 139-141 DOI:
[1] 郭建华,曾幸荣,罗权焜.橡胶阻尼减震材料的研究进展[J].特种橡胶制品,2002,33(6):68-72.
[2] 丁国芳,罗世凯,程青民,等.氯化丁基橡胶共混改性体系的力学阻尼性能研究[J].化工新型材料,2011,39(2):117-119.
[3] 孙志勇,马卫东,张鲲,等.氯化丁基橡胶阻尼材料动态力学性能的影响因素研究[J].世界橡胶工业,2009,36(1):19-20.
[4] 张榕,张德志,朱新生,宽温域高阻尼氯化丁基橡胶的制备及其阻尼与力学性能研究[J].苏州大学学报(工科版),2009,29(2):57-61.
[5] 王永刚,李超芹.炭黑填充丁基橡胶动态力学性能研究[J].世界橡胶工业,2010,37(10):10-14.
[6] 王永刚.宽温域高阻尼丁基橡胶材料的研究[D].青岛:青岛科技大学,2010.
[7] 张榕.氯化丁基橡胶阻尼材料的制备及性能研究[D].苏州:苏州大学,2009.