镍锰酸锂的固相法合成及结构分析

^2*

作者信息 +

Solid-phase synthesis and structure analysis of lithium nickel manganese oxide

Deng Bangjun¹, Yang Chun¹, Zhou Huanbo²

Author information +

文章历史 +

Received		Published
2016-06-01		2017-10-19
Issue Date	Revised Date
2017-10-19	2016-06-01

PDF

摘要

以二氧化锰、硝酸镍、碳酸锂为原料,采用固相法工艺合成了镍锰酸锂(LiNi_0.5Mn_1.5O₄)正极材料,采用X射线衍射仪(XRD)和扫描电子显微镜(SEM)对在不同焙烧温度、不同焙烧时间下制得的LiNi_0.5Mn_1.5O₄进行了表征。结果表明,900℃焙烧10h制得的LiNi_0.5Mn_1.5O₄的粒径约1μm,晶体结构完整,呈现规则的多面体形貌。

Abstract

Lithium nickel manganese oxide (LiNi_0.5Mn_1.5O₄) anode material was synthesized by solid phase method,using manganese dioxide,nickel nitrate and lithium carbonate as raw materials.X-ray diffraction (XRD) and scanning electron microscopy (SEM) were used to characterize the morphology and structure of LiNi_0.5Mn_1.5O₄ prepared under different calcination temperature and calcination time.The results showed that the as-prepared LiNi_0.5Mn_1.5O₄ samples were spinal crystals.The crystal structure of LiNi_0.5Mn_1.5O₄ calcinating at 900℃ for 10h was about 1μm complete crystal and the sample morphology was a regular polyhedron.

关键词

固相法 / 镍锰酸锂 / 正极材料

Key words

solid phase method / lithium nickel manganese oxide / anode material

引用本文

引用格式 ▾

镍锰酸锂的固相法合成及结构分析[J]. 化工新型材料, 2017, 45(9): 148-149 DOI:

登录浏览全文

4963

注册一个新账户忘记密码

参考文献

原文顺序 | 出版日期 | 本文引用

[1] 卢华权,吴锋,苏岳锋,等.5V锂离子电池正极材料LiNi_0.5Mn_1.5O₄的合成与Li⁺在材料中的扩散性能[J].高等学校化学学报,2011,32(4):946-951.[2] 李军,朱建新,李少芳,等.锂离子电池正极材料LiNi_0.5Mn_1.5O₄的固相法制备及性能研究[J].功能材料,2013,44(19):2796-2799.
[3] Fu Y P,Su Y H,Lin C H,et al.Comparison of microwave-induced combustion and solid-state reaction method for synthesis of LiMn_2-xCo_xO₄ powders and their electrochemical properties[J].Journal of Materials Science,2006,41(4):1157-1164.
[4] Zhu Z,Yan H,Zhang D,et al.Preparation of 4.7V cathode material LiNi_0.5Mn_1.5O₄ by an oxalic acid-pretreated solid-state method for lithium-ion secondary battery[J].Journal of Power Sources,2013,224(4):13-19.
[5] 牛甲明,郑宇亭,潘保武.锂离子电池正极材料尖晶石锰酸锂的研究进展[J].化工新型材料,2016,44(2):46-48.
[6] Park S H,Oh S W,Kang S H,et al.Comparative study of different crystallographic structure of LiNi_0.5Mn_1.5O_4-δ cathodes with wide operation voltage (2.0-5.0V)[J].Electrochemical Acta,2007,52(25):7226-7230.
[7] Wang L P,Li H,Huang X J,et al.A comparative study of Fd-3m and P4₃32 “LiNi_0.5Mn_1.5O₄”[J].Solid State Ionics,2011,193(1):32-38.

AI Summary AI Mindmap

PDF

410

访问

被引

导航

摘要

Abstract

关键词

Key words

中图分类号

引用本文

参考文献

AI思维导图