针对偏高岭土-水硬石灰砂浆材料抗拉强度低、极限延伸率小、性脆的问题,为了提高其韧性和稳定性,增强其抗裂能力,设计并制备了聚乙烯醇(PVA)纤维掺杂偏高岭土-水硬石灰砂浆材料,开展了PVA纤维不同掺量、不同长度下偏高岭土-水硬石灰砂浆材料收缩率、波速、抗压强度、抗折强度及劈裂抗拉强度的试验研究,通过扫描电镜观察分析了PVA纤维在偏高岭土-水硬石灰砂浆材料中的微观作用机理。结果表明:PVA纤维改变了偏高岭土-水硬石灰砂浆的收缩率和内部结构。试样的抗折强度和劈裂抗拉强度随着纤维增加而增大,抗压强度会在纤维长度一定时随着掺量的增多而降低。PVA纤维对砂浆材料整体性有明显改善,受压后仍能够保持着较好的原样性,纤维和砂浆基体之间产生了机械铆合作用,具有较好黏结性。
Aiming at the problems of metakaolin hydraulic lime mortar material,such as low tensile strength,low ultimate elongation and brittleness,in order to improve its toughness and stability,enhance its crack resistance,the PVA fiber doped metakaolin hydraulic lime mortar material was designed and prepared.The shrinkage rate,wave velocity,compressive strength,flexural strength and splitting tensile strength of the mortar with different content and length of PVA fiber were studied.The mechanism of PVA fiber in mortar was analyzed by SEM.The results shown that PVA fiber changed the shrinkage and internal structure of the mortar.The flexural strength and splitting tensile strength increased with increasing the fiber amount.The compressive strength decreased with increasing the fiber amount when the fiber length was constant.PVA fiber can obviously improve the integrity of mortar,and kep good original condition after compression.Mechanical riveting cooperation was developed between fiber and mortar,and had good adhesion.
[1] Ravi R,Thirumalini S.Effect of natural polymers from cissus glauca roxb on the mechanical and durability properties of hydraulic lime mortar[J].International Journal of Architectural Heritage,2018,13(11):1-15.
[2] Zhuang X S,Yu X Y.Experimental study on strength characteristics of lime-basalt fiber reinforced expansive soil[J].Applied Mechanics and Materials,2015,744-746:495-498.
[3] Maria L S,Francesca S,Martina Z,et al.Basalt fiber reinforced natural hydraulic lime mortars:a potential bio-based material for restoration[J].Materials & Design,2014,63:398-406.
[4] 袁勇,邵晓芸.合成纤维增强混凝土的发展前景[J].混凝土,2000(12):3-7.
[5] Reza B,Milad A,Ahmad F.Mechanical properties of steel and polymer fiber reinforced concrete[J].Journal of the Mechanical Behavior of Materials,2019,28(1):119-134.
[6] 高淑玲,徐世烺.PVA纤维增强水泥基复合材料拉伸特性试验研究[J].大连理工大学学报,2007,47(2):233-239.
[7] Prasanthni P,Palanisamy T.Mechanical characteristics and structural behaviour of engineered cementitious composites using polyvinyl alcohol fiber[J].Asian Journal of Research in Social Sciences and Humanities,2016,6(7):749-761.
[8] Tehmina A,Nasir S,Muhd F N.Analytical prediction of the mechanical properties of high performance PVA fiber reinforced concrete[J].Applied Mechanics and Materials,2014,3228:345-350.
[9] 高亚宁,史志杰,薛智刚.超高强度聚乙烯醇纤维的生产工艺研究[J].合成纤维,2006,35(6):36-38.
[10] 张景科,王南,樊孟,等.烧料礓石改性遗址土裂隙注浆材料龄期性能试验研究[J].岩石力学与工程学报,2018,37(1):220-229.
[11] Abu-Farsakh G A,Abdel-Jawad Y A,Abu-Laila K.Micromechanical characterization of tensile strength of fiber composite materials[J].Mechanics of Composite Materials & Structures,2000,7(1):105-122.
[12] 陈亚迪,洪丽,蒋津,等.水泥砂浆基体中玄武岩纤维的拔出试验研究[J].硅酸盐通报,2019,38(9):2985-2991.