以1,4-双(2′-三氟甲基-4′-氨基苯氧基)苯(6FAPB)和3,3′,4,4′-二苯醚四酸二酐(ODPA)为原料,N,N-二甲基乙酰胺(DMAc)为第一溶剂,丙酮为共溶剂,配制6种成分配比不同的制膜溶剂,然后采用热亚胺化法制成了6种聚酰亚胺薄膜。采用傅里叶红外光谱对其结构进行表征,并对其表面形貌、溶解时间、拉伸强度和热性能进行测试。结果表明:溶剂中添加丙酮制出来的薄膜,在有机溶剂中的溶解时间有着较大的区别。
1,4-bis(2′-trifluoromethyl-4′-aminophenoxy)benzene (6FAPB) and 3,3′,4,4′-diphenyl ether tetracarboxylic dianhydride (ODPA) used as raw materials,N,N-dimethylacetamide (DMAc)as the first solvent,acetone as the cosolvent,and six kinds of film-forming solvents having different distribution ratios were prepared,then six kinds of PI films were prepared by thermal imidization.The structure was characterized by fourier transform infrared spectroscopy,and its surface morphology,dissolution time,tensile strength and thermal properties were tested.The results shown that the dissolution time of the film prepared by adding acetone in the solvent had a big difference.
[1] 汪称意,赵辉鹏,李光,等.一种高可溶、高光学透明含氟聚酰亚胺的合成与表征[J].化学学报,2010,68(5):449-452.
[2] 尚雪亚,白俊敬.含芴基二胺单体及其聚酰亚胺的合成与表征[J].化工新型材料,2010,38(12):44-46.
[3] 安颢瑗,詹茂盛,王凯.含芴共聚聚酰亚胺胶黏剂的合成与性能研究[J].材料工程,2010(2):17-20.
[4] 刘金刚,陈建升,杨海霞,等.芴基取代耐高温聚酰亚胺的合成与性能[J].航空材料学报,2008(2):79-84.
[5] Tao L,Yang H,Liu J,et al.Synthesis and characterization of highly optical transparent and low dielectric constant fluorinated polyimides[J].Polymer,2009,50(25):6009-6018.
[6] Jin H S,Chang J H,Kim J C.Synthesis and characterization of colorless polyimide nanocomposite films containing pendant trifluoromethyl groups[J].Macromolecular Research,2008,16(6):503-509.
[7] Behniafar H,Sefid-Girandehi N.Optical and thermal behavior of novel fluorinated polyimides capable of preparing colorless,transparent and flexible films[J].Journal of Fluorine Chemistry,2011,132(11):878-884.
[8] Ghaemy M,Berenjestanaki F R,Organosoluble B M.Thermally stable and low diletric constant fluorinated polyimides containing 2,4,5-triphenylimidazole moiety in the main chains[J].Designed Monomers & Polymers,2014,17(2):101-110.
[9] Wang C,Chen W,Chen Y,et al.New fluorinated poly(ether sulfone imide)s with high thermal stability and low dielectric constant[J].Materials Chemistry & Physics,2014,143(2):773-778.
[10] Tong H,Hu C,Yang S,et al.Preparation of fluorinated polyimides with bulky structure and their gas separation performance correlated with microstructure[J].Polymer,2015,69:138-147.
[11] 尹大学,李彦锋,苏雅亭,等.可溶性聚酰亚胺共聚物的制备及其性能[J].化学通报,2005,68(10):781-784.
[12] 王亚平,李英芝,张清华.石墨烯/聚酰亚胺复合材料的制备与性能[J].高分子材料科学与工程,2013,29(12):144-147.
[13] See-Toh Y H,Ferreira F C,Living S A G.The influenceof membrane formation parameters on the functional performance of organic solvent nanofiltration mebranes[J].J Membr Sci,2007,299(1-2):236-250.