壳聚糖/Ti-W-V-Mn基金属氧化物复合脱硝催化剂的制备及性能研究

王新翠, 刘瑾, 李真, 王凯, 张定仑

doi:10.19817/j.cnki.issn 1006-3536.2020.07.049

化工新型材料 >

2020 , Vol. 48 >Issue 7: 215 - 220

DOI: https://doi.org/10.19817/j.cnki.issn 1006-3536.2020.07.049

科学研究

壳聚糖/Ti-W-V-Mn基金属氧化物复合脱硝催化剂的制备及性能研究

展开

1.安徽建筑大学材料与化学工程学院,合肥230022;
2.安徽省先进建筑材料重点实验室,合肥230022

王新翠(1993-),女,硕士研究生,主要研究方向为功能高分子与化学建材。

收稿日期: 2019-02-19

网络出版日期: 2022-11-01

基金资助

安徽省科技攻关项目(1604a0802113);国家自然科学基金项目(21171004);安徽省重点技术研究开发项目(1704a0802134)

收起

Synthesis and catalytic activity of CS/Ti-W-V-Mn oxide for ammonia-free SCR of NO

Expand

1. School of Materials Science and Chemical Engineering,Anhui Jianzhu University,Hefei 230022;
2. Anhui Key Laboratory of Advanced Building Materials,Anhui Jianzhu University,Hefei 230022

Received date: 2019-02-19

Online published: 2022-11-01

Fold

摘要

利用壳聚糖(CS)与Ti-W-V-Mn基金属氧化物复合制备新型选择性催化还原(SCR)催化剂CS/Ti-W-V-Mn,应用于NO的无氨辅助脱硝催化。采用SEM、FT-IR、XRD、BET及催化活性评价对催化剂的结构与性能进行表征。结果表明,CS/Ti-W-V-Mn复合脱硝催化剂不仅在低温区(180～250℃)具有良好的无氨催化脱硝性能,在高温区(350～400℃)仍具有较高的无氨脱硝活性。其中,当CS与Ti-W-V-Mn金基属氧化物的投料比(质量比)为1∶1时,催化性能最优,NO的转化率可在宽温度范围(180～400℃)内始终保持100%。该催化剂在低温无氨重复脱硝测试中仍具有较高的催化活性,可重复性较好。

关键词： 壳聚糖; Ti-W-V-Mn基金属氧化物; 无氨选择性催化还原; 催化脱硝

本文引用格式

王新翠, 刘瑾, 李真, 王凯, 张定仑 . 壳聚糖/Ti-W-V-Mn基金属氧化物复合脱硝催化剂的制备及性能研究[J]. 化工新型材料, 2020 , 48(7) : 215 -220 . DOI: 10.19817/j.cnki.issn 1006-3536.2020.07.049

Abstract

A novel ammonia-free denitrification catalyst was prepared by combining chitosan (CS) with Ti-W-V-Mn metal oxides.The structures and properties were characterized by scanning electron microscope (SEM),fourier transform infrared spectroscopy (FT-IR),X-ray diffraction (XRD) and microporous analyzer.And the catalytic denitrification activities of catalysts were collected by gas analyzer.The results indicated that the CS/Ti-W-V-Mn composite catalysts not only showed good catalytic activity at low temperature (180～250℃),but also performed well at high temperature (350～400℃).Especially,the NO conversion could up to 100% within 180～400℃ when the weight ratio between CS and Mn-V-W-Ti oxides was 1∶1 and it's repeatability of activity testing at low temperature without ammonia was good.

Key words： chitosan; Ti-W-V-Mn oxide; ammonia-free selective catalytic reduction(SCR); catalytic denitrification

参考文献

[1] 齐雪,陈红萍,杨旭.钛基SCR脱硝催化剂的研究进展[J].山东化工,2017,46(22):39-41.
[2] Gao R H,Zhang D S,Maitarad P,et al.Morphology-dependent properties of MnO_x/ZrO₂ CeO₂ nanostructures for the selective catalytic reduction of NO with NH₃[J].Journal of Physical Chemistry C,2013,117(20):10502-10511.
[3] 曹俊,周林,席文昌.SCR脱硝催化剂中毒的研究进展[J].应用化工,2018,47(2):380-385.
[4] 范晓丹,张襄楷,徐廷献.壳聚糖改性污泥活性炭的脱硫脱硝性能[J].环境科学学报,2012,32(7):1750-1756.
[5] 张奎,王悦,孙雪晴,等.FeZSM-5骨架调控及其对NO_x的SCR性能研究[J].合成化学,2018,26(1):9-14.
[6] 高岩,栾涛,彭吉伟,等.四元SCR催化剂V₂O₅-WO₃-MoO₃/TiO₂脱硝性能[J].功能材料,2013,44(14):2092-2096.
[7] 杨佳,李平,王姝.SCR脱硝催化剂的制备方法[J].化工管理,2015,8(23):11-12.
[8] 尚玉婷,陈莉.壳聚糖-TiO₂复合絮凝剂的制备及其在印染废水处理中的应用[J].天津工业大学学报,2013,32(3):56-60.
[9] 陈伟,廖卫平,金明善,等.壳聚糖修饰炭黑负载Pt-Au催化剂对甲醇氧化的电催化性能[J].燃料化学学报,2012,40(12):1459-1465.
[10] 云亮,刘峥,李海莹,等.壳聚糖原位合成复合炭材料及表征[J].炭素技术,2016,35(6):28-32.
[11] 王爱勤,赵培庆,高小军,等.壳聚糖与不同金属锌盐配位的红外光谱研究[J].光谱学与光谱分析,1999,19(6):817-820.
[12] 赵国骏,姜涌明,孙龙生,等.不同来源壳聚糖的基本特性及红外光谱研究[J].功能高分子学报,1998,11(3):403-407.
[13] 郭静,李彩亭,路培,等.CeO₂改性MnO_x/Al₂O₃的低温SCR法脱硝性能及机制研究[J].环境科学,2011,32(8):2240-2246.

Options

文章导航

模态框（Modal）标题

摘要

本文引用格式

Abstract

参考文献