新型有机-无机复合相变蓄冷材料的制备及性能研究
曹士博, 罗孝学*, 韩晓春, 邹长贞, 蓝广林
北部湾大学,钦州535011
Preparation and properties of novel organic-inorganic composite phase change cold storage materials
Cao Shibo, Luo Xiaoxue, Han Xiaochun, Zou Changzhen, Lan Guanglin
Beibu Gulf University,Qinzhou 535011
下载: 
输出:  BibTeX | EndNote (RIS)      
摘要 以六水氯化钙为基材,配备出一种新型复合相变蓄冷材料用于空调蓄冷。该材料的质量配比为81%六水氯化钙+5%乙醇+14%丙三醇。为了降低复合相变材料的过冷度,使用六水氯化铯为成核剂,发现成核剂的添加量为1.0%时过冷度几乎为零。为检验复合相变材料的热稳定性,进行了100次的热循环实验,材料未出现相分层,表明其热稳定性能良好。
服务
把本文推荐给朋友
加入引用管理器
E-mail Alert
RSS
作者相关文章
曹士博
罗孝学
韩晓春
邹长贞
蓝广林
关键词:  复合相变材料  六水氯化钙  乙醇  丙三醇  蓄冷    
Abstract: With CaCl2·6H2O as the base material,a new type of composite phase change cold storage material was prepared for air-conditioning cold storage.The mass ratio of the material was 81wt.% calcium chloride hexahydrate+5wt.% ethanol+14wt.% glycerol.In order to reduce the undercooling of composite phase change materials,cesium chloride hexahydrate was used as nucleating agent.It was found that the undercooling was almost zero when the amount of nucleating agent was 1.0wt.%.Aiming to test the thermal stability of the composite phase change material,100 thermal cycling experiments were carried out,and the material did not show phase stratification,indicating that its thermal stability was good.
Key words:  composite phase change materials (CPCM)    calcium chloride hexahydrate    ethanol    glycerol    cold storage
收稿日期:  2022-01-22      修回日期:  2023-02-18           出版日期:  2023-05-20      发布日期:  2023-05-31     
ZTFLH:  TK02  
基金资助: 广西自然科学基金面上项目(2018GXNSFAA138157);广西科技基地和人才专项(桂科AD18281082);钦州学院高层次人才科研启动经费项目(2017KYQD210)
通讯作者:  罗孝学(1978-),男,博士,副教授,主要从事新能源蓄能领域研究工作,E-mail:lxx138916@bbgu.edu.cn。   
作者简介:  曹士博(1998-),男,硕士研究生,主要从事新能源蓄能领域研究工作。
引用本文:    
曹士博, 罗孝学, 韩晓春, 邹长贞, 蓝广林. 新型有机-无机复合相变蓄冷材料的制备及性能研究[J]. 化工新型材料, 2023, 51(5): 68-72.
Cao Shibo, Luo Xiaoxue, Han Xiaochun, Zou Changzhen, Lan Guanglin. Preparation and properties of novel organic-inorganic composite phase change cold storage materials. New Chemical Materials, 2023, 51(5): 68-72.
链接本文:  
https://www.hgxx.org/CN/10.19817/j.cnki.issn1006-3536.2023.05.012  或          https://www.hgxx.org/CN/Y2023/V51/I5/68
[1] 郭丽佳,李畅,彭红松,等.节能减排约束下中国省域旅游生态效率评估及空间格局研究[J].地理科学进展,2021,40(8):1284-1297.
[2] 章慧颖.冷冻水变流量系统节能性分析[J].应用能源技术,2020(7):46-48.
[3] 张茜,王宇,安允,等.动态冰浆系统安装与调试技术[J].洁净与空调技术,2021(4):16-18.
[4] 罗孝学,邹长贞.一种用于储存太阳能的相变材料研究[J].太阳能,2018(1):62-66.
[5] 罗孝学,章学来,华维三,等.脉动热管相变蓄热器蓄热实验分析[J].化工学报,2017,68(7):2722-2729.
[6] Lu X,Luo X,Cao S,et al.Experimental analysis on heat release of pulsating heat pipe phase change regenerator with different working fluids[C].Journal of Physics:Conference Series.IOP Publishing,2021,2087(1):012008.
[7] Nagano K,Ogawa K,Mochida T,et al.Thermal characteristics of magnesium nitrate hexahydrate and magnesium chloride hexahydrate mixture as a phase change material for effective utilization of urban waste heat[J].Applied Thermal Engineering,2004,24(2-3):221-232.
[8] 杨颖,沈海英.复合低温相变蓄冷材料的实验研究[J].低温物理学报,2009,31(2):144-147.
[9] 李靖,谢如鹤,刘广海,等.冷藏运输用新型低温相变材料及装备的研制[J].制冷学报,2018,39(4):32-37.
[10] Wang X,Dennis M,Hou L.Clathrate hydrate technology for cold storage in air conditioning systems[J].Renewable & Sustainable Energy Reviews,2014,36:34-51.
[11] Telkes M.Nucleation of supersaturated inorganic salt solutions[J].Arthritis Care & Research,1952,13(6):112.
[12] 李晓燕,周维,周辉.适用与蓄冷空调的二元相变蓄冷材料的测试与研究[J].哈尔滨商业大学学报(自然科学版),2001(4):108-110.
[13] Zou T,Fu W,Liang X,et al.Preparation and performance of form-stable TBAB hydrate/SiO2 composite PCM for cold energy storage[J].International Journal of Refrigeration,2019,101:117-124.
[14] Kenisarin M,Mahkamov K.Salt hydrates as latent heat storage materials:thermophysical properties and costs[J].Solar Energy Materials & Solar Cells,2016,145:255-286.
[15] Lane D G.Low temperature heat storage with phase change materials[J].International Journal of Ambient Energy,2011(3):155-168.
[16] Zhang X X,Zhou Y,Xiang L,et al.Research progress of calcium chloride hexahydrate phase change material[J].Energy Storage Science and Technology,2018,7(1):40-47.
[17] Tyagi V V,Buddhi D.Thermal cycle testing of calcium chloride hexahydrate as a possible PCM for latent heat storage[J].Solar Energy Materials & Solar Cells,2008,92(8):891-899.
[18] Zhang X,Zhou S,Liu S,et al.Cold storage characteristics of n-octanoic-lauric acid nanocomposite phase change materials[J].Journal of Tianjin University Science and Technology,2019,52(1):71-77.
[19] Zhang S,Zhang X,Xu X,et al.Preparation and properties of decyl-myristyl alcohol/expanded graphite low temperature composite phase change material[J].Phase Transitions,2020,93(14):1-13.
[20] Lane G A.Phase change materials for energy storage nucleation to prevent supercooling[J].Solar Energy Materials & Solar Cells,1992,27(2):135-60.
[21] 李志广,徐雷,黄红军,等.相变恒温材料六水氯化钙的研究[C].第六届中国功能材料及其应用学术会议论文集,2007:241-242.
[22] 刘超.六水氯化钙重结晶的相分层机理和控制研究[J].中国建材科技,2015,24(3):52-53.
[1] 曾军, 李翔晟, 欧阳立芳, 李藏龙, 张心成, 陈志峰. 石蜡/膨胀石墨/碳化硅复合相变材料的制备及热性能研究[J]. 化工新型材料, 2023, 51(4): 115-118.
[2] 徐众, 吴恩辉, 侯静, 李军, 昝学平. 不同支撑材料/PEG-1500复合相变材料的制备及热性能研究[J]. 化工新型材料, 2023, 51(4): 275-280.
[3] 常洋珲, 孙志高. 十二醇-十六醇-辛酸三元复合相变材料的制备及性能研究[J]. 化工新型材料, 2022, 50(9): 139-143.
[4] 欧阳立芳, 郭美华, 李翔晟, 陈志峰, 王雨妍, 李藏龙. EG-CF/PW三元复合相变材料的制备及热特性分析[J]. 化工新型材料, 2022, 50(5): 146-150.
[5] 闫嘉森, 李建刚, 何向明. 固-液转化形相变蓄冷材料的研究进展[J]. 化工新型材料, 2022, 50(4): 241-246.
[6] 黄菊花, 陈强, 曹铭, 刘自强, 胡金. 石蜡/膨胀石墨/石墨烯/铝蜂窝复合相变材料的制备及锂电池控温性能研究[J]. 化工新型材料, 2022, 50(2): 140-144.
[7] 闫全英, 马广园, 王威. 脂肪酸/石蜡/石墨复合相变材料对不锈钢的腐蚀性研究[J]. 化工新型材料, 2022, 50(12): 96-98.
[8] 王海涛, 李建, 李皖皖. 基于PA/OBC/EG复合相变材料的锂离子电池热管理研究[J]. 化工新型材料, 2022, 50(11): 141-146.
[9] 秦威南, 何强, 祝强, 朱凯, 贺兰山, 江川. 相变蓄冷材料研究进展[J]. 化工新型材料, 2021, 49(5): 1-6.
[10] 徐众, 侯静, 李军, 吴恩辉, 黄平. 提钒尾渣对膨胀石墨/石蜡复合相变材料导热性能的影响[J]. 化工新型材料, 2021, 49(5): 115-119.
[11] 吴学红, 王强伟, 王凯, 高磊, 刘鹤, 王长学, 王怡滢. 纳米粒子强化有机复合相变材料的热物性及其应用研究进展[J]. 化工新型材料, 2021, 49(4): 40-45.
[12] 黄菊花, 胡金, 曹铭, 刘自强, 姜贵文. 复合相变材料制备及其与散热片耦合控温性能研究[J]. 化工新型材料, 2021, 49(4): 103-107.
[13] 刘晨敏. 冷链物流用复合相变蓄冷材料研究进展[J]. 化工新型材料, 2021, 49(2): 16-19.
[14] 陈志能, 丁辉, 吴淑英, 陈丹丹. 基于复合相变散热的锂离子电池热管理实验研究[J]. 化工新型材料, 2021, 49(2): 144-148.
[15] 张托弟, 王毅, 张宇, 王建君, 沈玉霞. 黏土矿物基定形复合相变材料储热性能的研究进展[J]. 化工新型材料, 2021, 49(12): 50-54.
No Suggested Reading articles found!
Viewed
Full text


Abstract

Cited

  Shared   
  Discussed   
京ICP备09035943号-38
版权所有 © 《化工新型材料》编辑部
本系统由北京玛格泰克科技发展有限公司设计开发 技术支持:support@magtech.com.cn