化工新型材料  2019, Vol. 47 Issue (5): 127-130    
  科学研究 本期目录 | 过刊浏览 | 高级检索 |
低温复合相变材料正辛酸-癸酸的制备及性能分析
李玉洋, 章学来*, Jotham Muthoka Munyalo, 王迎辉, 周孙希
上海海事大学蓄冷技术研究所,上海201306
Preparation and characterization of low temperature binary composite PCM N-caprylic acid and capric acid
Li Yuyang, Zhang Xuelai, Jotham Muthoka Munyalo, Wang Yinghui, Zhou Sunxi
Institute of Cool Storage Technology,Shanghai Maritime University,Shanghai 201306
下载:  PDF (1486KB) 
输出:  BibTeX | EndNote (RIS)      
摘要 将正辛酸(OA)与癸酸(CA)按比例混合制备二元复合相变材料OA-CA,用于相变温度2~8℃的医药冷藏运输系统中。首先通过理论计算预测了二元混合物的共晶点,确定它的共晶点比例、相变温度及潜热值,然后围绕共晶点比例配制6种不同比例的混合物。结果表明:OA-CA的过冷度为0.4℃、共晶点质量比为71∶29、相变温度为1.7℃、相变潜热为122.1J/g、热导率为0.3231W/(m·K)。对OA-CA低温复合相变材料进行100次循环蓄放冷实验,发现其相变温度、潜热值、热导率均未发生明显变化。
服务
把本文推荐给朋友
加入引用管理器
E-mail Alert
RSS
作者相关文章
李玉洋
章学来
Jotham Muthoka Munyalo
王迎辉
周孙希
关键词:  二元混合物  相变材料  热性能  循环  稳定性    
Abstract: The binary composite phase change material N-caprylic acid (OA) and Caprylic acid (CA) were mixed in proportion,for phase change temperature in 2~8℃ medical refrigerating transportation system.Firstly,the eutectic point of binary mixture was predicted by theoretical calculation,and the eutectic point ratio,phase change temperature and latent heat were determined.Then six kinds of different proportion of mixture around the eutectic point were made.The experimental results showed that the super-cooling degree of OA-CA was 0.4℃.At the eutectic point,the mass ratio was 71∶29 and the phase transition temperature was 1.7℃.The latent heat of fusion was found to be 122.1J/g and the thermal conductivity was 0.3231W/(m·K).It was found that the phase change temperature,latent heat,thermal conductivity of OA-CA composite phase change material were not significantly changed after 100 cycles of cold storage experiment.
Key words:  binary mixture    phase change material    thermal property    recycling    stability
收稿日期:  2017-12-22                     发布日期:  2019-06-17      期的出版日期:  2019-05-20
基金资助: 上海市科委项目(16040501600)
通讯作者:  章学来(1964-),男,教授,博士,博士研究生导师,主要从事蓄能技术研究。   
作者简介:  李玉洋(1993-),男,硕士,主要研究方向为冷链物流。
引用本文:    
李玉洋, 章学来, Jotham Muthoka Munyalo, 王迎辉, 周孙希. 低温复合相变材料正辛酸-癸酸的制备及性能分析[J]. 化工新型材料, 2019, 47(5): 127-130.
Li Yuyang, Zhang Xuelai, Jotham Muthoka Munyalo, Wang Yinghui, Zhou Sunxi. Preparation and characterization of low temperature binary composite PCM N-caprylic acid and capric acid. New Chemical Materials, 2019, 47(5): 127-130.
链接本文:  
http://www.hgxx.org/CN/  或          http://www.hgxx.org/CN/Y2019/V47/I5/127
[1] 黄雪,崔英德,尹国强,等.月桂酸-膨胀石墨复合相变材料的制备及性能[J].化工学报,2015,66(S1):370-374.
[2] 孙文鸽,韩磊,吴志根.膨胀石墨/石蜡相变复合材料有效导热系数的数值计算[J].复合材料学报,2015,32(6):1596-1601.
[3] 吕学文,考宏涛,李敏.膨胀石墨/石蜡复合相变材料相变过程的热分析[J].材料导报,2011,25(2):131-134.
[4] 黄艳,章学来.十二醇-癸酸纳米粒子复合相变材料传热性能[J].化工学报,2016,67(6):2271-2276.
[5] Taguchi Y,Yokoyama H,Kado H,et al.Preparation of PCM-microcapsules by using oil absorbable polymer particles[J].Colloids Surf A:Phys Eng Aspects,2007,301(7):5-41.
[6] 于永生,井强山,孙雅倩.低温相变储能材料研究进展[J].化工进展,2010,29(5):896-900,913.
[7] 章学来,杨阳.月桂酸-正辛酸低温相变材料的制备和循环性能[J].化学工程,2013,41(11):10-14.
[8] 袁艳平,白力,牛犇.脂肪酸二元低共熔混合物相变温度和潜热的理论预测[J].材料导报,2010,24(1):111-113.
[9] Zhang N,Yuan Y P,Yuan Y G,et al.Effect of carbon nanotubes on the thermal behavior of palmitic-stearic acid eutectic mixtures as phase change materials for energy storage[J].Sol Energy,2014,110:64-70.
[10] Liu C,Yuan Y P,Zhang N,et al.A novel PCM of lauric-myristic-stearic acid/expanded graphite composite for thermal energy storage[J].Mater Lett,2014,120:43-46.
[11] Yuan Y G,Yuan Y P,Zhang N.Preparation and thermal characterization of capric-myristic-palmitic acid/expanded graphite composite as phase change material for energy storage[J].Mater Lett,2014,125:154-157.
[12] Zhang N,Yuan Y P,Yuan Y G.Lauric-palmitic-stearic acid/expanded perlite composite as form-stable phase change material:preparation and thermal properties[J].Energ Buildings,2014,82:505-511.
[13] Yuan Y P,Zhang N,Tao W Q,et al.Fatty acids as phase changematerials:a review[J].Renew Sust Energ Rev,2014,29:482-498.
[14] Zhang N,Yuan Y P,Wang X,et al.Preparation and characterization of lauric-myristic-palmitic acid ternary eutectic mixtures/expanded graphite composite phase change material for thermal energy storage[J].Chemical Engineering Journal,2013,231:214-219.
[15] 袁艳平,白力,牛犇.癸酸与棕榈酸低共熔混合物的制备与热特性分析[J].材料导报,2010,24(8):113-115.
[16] 刘程,袁艳平,张楠,等.脂肪酸三元低共熔混合物相变温度和潜热的理论预测[J].材料导报,2014,28(2):165-168.
[17] 邹得球,詹建,李乐园,等.热水器用相变储热材料的研究进展[J].化工进展,2017,36(1):268-273.
[18] 陈文朴,章学来,丁锦宏,等.癸酸-正辛酸低温相变材料的制备和循环性能[J].制冷学报,2016,37(3):12-16.
[19] 张寅平,苏跃红,葛新石.(准)共晶系相变材料融点及融解热的理论预测[J].中国科学技术大学学报,1995,25(4):475-476.
[20] 胡孝才,吴会君,周孝清.十二醇/辛酸二元混合工质相变蓄冷过程结晶特性[J].广州大学学报(自然科学版),2011,10(2):60-62.
[1] 杨昊天, 蒋达华, 张鑫林, 廖绍璠, 费华, 刘兰华. 硅藻土基相变储能调湿材料的应用研究进展[J]. 化工新型材料, 2019, 47(5): 32-35.
[2] 李覃, 李斌, 李帅臻, 赵梁成. 碳系填充型导电聚氨酯弹性体性能研究[J]. 化工新型材料, 2019, 47(5): 68-72.
[3] 易波, 赵运涛, 李静, 田恩玲, 任以伟. 电纺聚酰亚胺/氧化石墨烯复合纳米纤维膜的制备及性能研究[J]. 化工新型材料, 2019, 47(5): 64-67.
[4] 严石静, 王雷, 栾安博, 麦裕良. 端硅烷基聚醚树脂的合成及其储存稳定性[J]. 化工新型材料, 2019, 47(5): 81-84.
[5] 王趁义, 王国贺, 王凤玲, 郝琦玮, 瞿帆. 氧化石墨烯改性聚(丙烯酸/丙烯酰胺)高吸水树脂的制备及性能研究[J]. 化工新型材料, 2019, 47(5): 90-95.
[6] 班超方, 卢立新, 潘 嘹. 冷冻型复合相变蓄冷材料的制备与性能评价[J]. 化工新型材料, 2019, 47(5): 218-221.
[7] 李新. 相变调温材料对沥青及沥青混合料高温性能及控温性能的影响探究[J]. 化工新型材料, 2019, 47(5): 253-256.
[8] 李振, 刘素美, 贾兰, 陈松, 朱晶心. 丝素蛋白包裹的银纳米粒子稳定性及抗菌性研究[J]. 化工新型材料, 2019, 47(5): 264-268.
[9] 郑少娜,马冠豪,郑杭冰,胡光杰,周杨,王海林,廖文波. 含氟苯丙聚合物/二茂铁复合涂层疏水性能调控[J]. 化工新型材料, 2019, 47(4): 145-148.
[10] 朱阳倩,汪海平. 壁材掺杂纳米TiO2的正十四醇相变微胶囊的制备及性能研究[J]. 化工新型材料, 2019, 47(3): 134-137.
[11] 柳滢春, 郭建维, 罗涛, 王伟彬. 链式(2,7-咔唑)-金刚烷共聚物的合成及性能研究[J]. 化工新型材料, 2019, 47(2): 77-81.
[12] 任瑞. PEG/TiO2/石墨烯复合相变材料的制备及其在沥青改性中的应用探究[J]. 化工新型材料, 2019, 47(2): 219-222.
[13] 唐云雨, 徐芬, 孙立贤, 夏永鹏, 陈冬梅, 兰孝征. 纳米限域的十四醇相变材料的相变行为研究[J]. 化工新型材料, 2019, 47(2): 162-165.
[14] 尹术帮, 赵凯, 杨杰. 核壳橡胶纳米粒子改性环氧树脂/酸酐体系固化动力学及其性能研究[J]. 化工新型材料, 2019, 47(2): 180-183.
[15] 朱胜兰, 李莎莎, 邹伟, 杨虎, 颜杰, 李斌. 无表面活性剂全氟聚醚基磁流体的开发研究[J]. 化工新型材料, 2019, 47(1): 156-159.
No Suggested Reading articles found!
Viewed
Full text


Abstract

Cited

  Shared   
  Discussed   
京ICP备09035943号-38
版权所有 © 《化工新型材料》编辑部
本系统由北京玛格泰克科技发展有限公司设计开发 技术支持:support@magtech.com.cn