TiO2改性PVDF锂离子电池隔膜的研究
李琳1,2, 陈建1,2*, 龚勇1,2, 刘平1,2, 代祖洋1,2, 辜其隆1,2
1.四川理工学院材料科学与工程学院,自贡643000;
2.材料腐蚀与防护四川省重点实验室,自贡643000
Study on TiO2 modified PVDF lithium ion battery separator
Li Lin1,2, Chen Jian1,2, Gong Yong1,2, Liu Ping1,2, Dai Zuyang1,2, Gu Qilong1,2
1.College of Materials Science and Engineering,Sichuan University of Science & Engineering,Zigong 643000;
2.Sichuan Province Key Laboratory for Corrosion and Protection of Material,Sichuan University of Science & Engineering,Zigong 643000;
下载:  PDF (2231KB) 
输出:  BibTeX | EndNote (RIS)      
摘要 静电纺丝制备聚偏氟乙烯(PVDF)锂离子电池隔膜电化学性能一般,可采用混纺增强其电化学性能。采用二氧化钛(TiO2)与PVDF混纺,制得TiO2/PVDF锂离子电池隔膜,研究不同TiO2的添加量对TiO2/PVDF锂离子电池隔膜性能的影响,考察其力学性质、离子电导率、放电比容量和循环性能。结果表明:在添加1.5%(wt,质量分数)TiO2条件下,制得的TiO2/PVDF锂离子电池隔膜的孔隙率高达52.54%,吸液率403.70%,离子电导率4.2×10-4S/cm;在0.5C条件下放电比容量为134.0mAh/g,循环25次条件下,TiO2/PVDF锂离子电池隔膜的放电比容量仍有130.0mAh/g,放电比容量的波动小,循环稳定性好。
服务
把本文推荐给朋友
加入引用管理器
E-mail Alert
RSS
作者相关文章
李琳
陈建
龚勇
刘平
代祖洋
辜其隆
关键词:  静电纺丝  锂离子电池隔膜  聚偏氟乙烯  TiO2    
Abstract: The electrochemical properties of PVDF lithium ion battery separators prepared by electrospinning were general,but it can be enhanced by blending.TiO2/PVDF separator was prepared by blending titanium dioxide (TiO2) with PVDF.The effects of different TiO2 addition on the performance of TiO2/PVDF and its mechanical properties,ionic conductivity,discharge capacity and cycle performance were also investigated.The results showed that when added TiO2 of 1.5wt%(wt,mass fraction),the porosity of TiO2/PVDF reached 52.54%,the electrolyte uptake reached 403.70%,and the ion conductivity reached 4.2×10-4S/cm.The discharge capacity was 134.0mAh/g at the rate of 0.5C,the discharge still remained 130mAh/g after 25 cycles,the fluctuation of discharge capacity was small,and the cycle stability was good.
Key words:  electrospinning    Li-ion battery separator    polyvinylidene fluoride(PVDF)    TiO2
收稿日期:  2017-08-02                     发布日期:  2019-01-07      期的出版日期:  2018-12-20
基金资助: 国家自然科学基金面上项目(51572177);四川省科技厅项目(2016GZ0224);四川省科技厅项目(2017JY0158);材料腐蚀与防护四川省重点实验室开放基金项目(2017CL12)
通讯作者:  陈建(1963-),男,教授,研究方向为化工新型材料。   
作者简介:  李琳(1993-),女,在读硕士,主要从事高分子材料的研究。
引用本文:    
李琳, 陈建, 龚勇, 刘平, 代祖洋, 辜其隆. TiO2改性PVDF锂离子电池隔膜的研究[J]. 化工新型材料, 2018, 46(12): 133-136.
Li Lin, Chen Jian, Gong Yong, Liu Ping, Dai Zuyang, Gu Qilong. Study on TiO2 modified PVDF lithium ion battery separator. New Chemical Materials, 2018, 46(12): 133-136.
链接本文:  
http://www.hgxx.org/CN/  或          http://www.hgxx.org/CN/Y2018/V46/I12/133
[1] Qin Y.Micro-manufacturing engineering and technology[J].Micro-Manufacturing Engineering and Technology,2010,21(3):1-23.
[2] 罗少伶,陈建,胥会,等.静电纺丝制备聚酰亚胺无纺布纤维膜工艺及性能研究[J].四川理工学院学报,2016,29(3):9-13.
[3] Lysenko V A,Druzhinina T V,Lysenko A A,et al.Carbon-carbon composites based on precursors obtained by electrostatic;spinning[J].Fibre Chemistry,2013,45(1):21-24.
[4] Zhang J,Yue L,Kong Q,et al.Sustainable,heat-resistant and flame-retardant cellulose-based composite separator for high-performance lithium ion battery[J].Scientific Reports,2014,4(1):2411-2502.
[5] 李丽叶,刘鹏程,朱孔军.静电纺丝法制备硅碳纳米纤维及其在锂钠离子电池中的应用[J].新能源进展,2016,4(6):443-454.
[6] Chen T,Liu Y,Pan L,et al.Electrospun carbon nanofibers as anode materials for sodium ion batteries with excellent cycle performance[J].Journal of Materials Chemistry A,2014,2(12):4117-4121.
[7] Shin J,Park K,Ryu W H,et al.Graphene wrapping as a protective clamping layer anchored to carbon nanofibers encapsulating Si nanoparticles for a Li-ion battery anode[J].Nanoscale,2014,6(21):12718-12726.
[8] Li W,Zeng L,Yang Z,et al.Free-standing and binder-free sodium-ion electrodes with ultralong cycle life and high rate performance based on porous carbon nanofibers[J].Nanoscale,2013,6(2):693-698.
[9] 师奇松,于建香,顾克壮,等.静电纺丝技术及其应用[J].化学世界,2005,46(5):313-316.
[10] 吴大钊.PVdF-HFP基锂离子电池隔膜增强改性研究[D].苏州:苏州大学,2015.
[11] 贾恒义.锂离子电池材料的研究与应用[J].电源技术,2011(7):869-871.
[12] Yang P,Su Jinran.Technology and application progress of lithium ion battery[J].Chinese Journal of Power Sources,2009,33(11):1037-1039.
[13] 赵剑蒙.锂离子电池用PVDF/PMMA静电纺复合隔膜的制备与改性研究[D].上海:东华大学,2014.
[14] 李春艳.PVDF电纺纤维膜的成型及其性能研究[D].广州:华南理工大学,2014.
[15] 李宸.TiO2纳米粒子改性PVDF/PMMA复合薄膜的制备及性质[D].上海:东华大学,2013.
[16] 宗云鹏.一维多孔结构TiO2纤维的制备及其在锂电池中的应用[D].沈阳:沈阳航空航天大学,2016.
[1] 关恩昊, 岳红彦, 高鑫, 王宝, 王婉秋, 王钊, 宋姗姗, 张宏杰. TiO2纳米线(管)-石墨烯的制备方法和应用现状[J]. 化工新型材料, 2018, 46(9): 13-16.
[2] 何一鸣, 郭学彬, 孙晓芳, 王新爽, 展侠, 李继定. 加成型硅橡胶复合膜的制备及渗透汽化性能研究[J]. 化工新型材料, 2018, 46(9): 84-87.
[3] 王其智, 汪滨, 王娇娜, 漆麟, 李从举. 基于静电纺-层层组装技术制备[壳聚糖/海藻酸钠]c/l/聚乙烯醇纳米复合膜[J]. 化工新型材料, 2018, 46(9): 140-143.
[4] 张金宁, 宋明玉, 陈昀, 曹建华, 杨占平, 徐阳, 魏取福. 二醋酸/有机改性蒙脱土复合多孔纤维的制备及其染料吸附性能[J]. 化工新型材料, 2018, 46(9): 144-147.
[5] 贾济如, 王潮霞, 殷允杰. 静电纺丝法制备吲哚美辛纳米粒子/聚乙烯醇复合纤维膜[J]. 化工新型材料, 2018, 46(9): 88-90.
[6] 张艺萌, 彭程程, 张权, 徐阳, 王清清. PVA-SbQ/透明质酸复合纳米纤维的制备及表征[J]. 化工新型材料, 2018, 46(8): 231-233.
[7] 熊乐艳, 张楠, 郭赞如, 马伟, 郑龙珍. 掺N纳米TiO2光催化材料的制备及其光催化性能研究[J]. 化工新型材料, 2018, 46(8): 97-101.
[8] 刘玥波, 王娇娜, 汪滨, 李从举. 静电纺PA56纳米纤维膜的制备及力学性能研究[J]. 化工新型材料, 2018, 46(8): 149-152.
[9] 张明玉, 蔡文迪, 孙岚, 张正中. 微波烧结法制备羟基磷灰石/TiO2复合涂层[J]. 化工新型材料, 2018, 46(8): 166-169.
[10] 田林, 黄俊, 李荣兴, 李威, 谢刚, 杨妮, 俞小花. 氯化法制备纳米TiO2氧化机理的研究进展[J]. 化工新型材料, 2018, 46(8): 238-243.
[11] 黄云镜, 于计生, 唐丽梅, 李青松. 太阳光下TiO2光催化还原Cr(Ⅵ)影响因素研究[J]. 化工新型材料, 2018, 46(8): 191-194.
[12] 孟亚飞, 裴广玲. 静电纺纳米纤维膜处理重金属离子污水研究进展[J]. 化工新型材料, 2018, 46(8): 281-284.
[13] 金奇杰, 潘有春, 陶兴军, 沈岳松, 祝社民. Al3+掺入对CeO2(ZrO2)/TiO2催化剂脱硝性能的影响[J]. 化工新型材料, 2018, 46(7): 227-231.
[14] 林春玲, 焦小妮, 周玲, 常木蓝, 刘明杰. 水热法制备氧化石墨烯负载TiO2的研究[J]. 化工新型材料, 2018, 46(7): 81-84.
[15] 张敬, 孙学凤, 高婷婷, 周国伟. TiO2/MoS2复合材料的制备及其在光催化和储能电池中的应用研究进展[J]. 化工新型材料, 2018, 46(6): 43-47.
No Suggested Reading articles found!
Viewed
Full text


Abstract

Cited

  Shared   
  Discussed   
京ICP备09035943号-38
版权所有 © 《化工新型材料》编辑部
本系统由北京玛格泰克科技发展有限公司设计开发 技术支持:support@magtech.com.cn