尿素对聚己内酯二醇结晶性能的影响研究
王婉婉, 陈红祥*, 代巧丽, 赵丹, 王丽娟, 周瑜, 曾丹林
武汉科技大学化学与化工学院,煤转化与新型炭材料湖北省重点实验室,武汉430081
Influence of urea on crystallization of polycaprolactone
Wang Wanwan, Chen Hongxiang, Dai Qiaoli Zhao Dan, Wang Lijuan, Zhou Yu, Zeng Danlin
Hubei Province Key Laboratory of Coal Conversion and New Carbon Materials,School of Chemistry and Chemical Engineering,Wuhan University of Science and Technology,Wuhan 430081
下载:  PDF (4365KB) 
输出:  BibTeX | EndNote (RIS)      
摘要 通过添加小分子尿素制备了聚己内酯(PCL)/尿素复合物,以期改变PCL的结晶性能。利用显微熔点、X射线衍射(XRD)、差示扫描量热法(DSC)、偏光显微镜(POM)等手段研究了PCL/尿素复合物的熔程、结晶度、结晶形态以及结晶过程,通过傅里叶变换红外光谱仪分析了PCL/尿素复合物的结构。结果表明:PCL及其复合物的结晶形态均为球晶,复合物球晶的密集程度较纯PCL明显增加,随着尿素含量增加,球晶尺寸变小;PCL/尿素复合物的结晶度相比纯PCL略有降低;尿素的加入使PCL熔程变窄。这是由于尿素与PCL间产生了氢键,并起到了成核剂的作用。
服务
把本文推荐给朋友
加入引用管理器
E-mail Alert
RSS
作者相关文章
王婉婉
陈红祥
代巧丽
赵丹
王丽娟
周瑜
曾丹林
关键词:  聚己内酯  尿素  结晶    
Abstract: PCL/urea complex was prepared by adding small molecular urea to improve the crystallinity of PCL.The melting range,crystallinity,crystal morphology and crystallization process of complex were studied by micro-melting point,X-ray diffraction (XRD),differential scanning calorimetry (DSC) and polarizing microscopy (POM).The structure of complexe was studied by fourier transform infrared spectroscopy (FT-IR).The results showed that the crystal morphology of PCL and its complex were spherulite,and the density of spherulite in complex was higher than pure PCL.The size of spherulite became smaller with the increase of urea content.The crystallinity of complex was slightly lower than pure PCL.The adding of urea narrowed the melting range of PCL.This was due to the hydrogen bonding between urea and PCL,and urea played a role in the nucleating agent.
Key words:  polycaprolactone    urea    crystallization
收稿日期:  2017-07-28                出版日期:  2018-11-20      发布日期:  2018-12-04      期的出版日期:  2018-11-20
基金资助: 国家自然科学基金(21473126)
通讯作者:  陈红祥(1974-),男,教授,主要从事高分子材料研究。   
作者简介:  王婉婉(1992-),女,硕士研究生,主要从事智能聚氨酯材料研究工作。
引用本文:    
王婉婉, 陈红祥, 代巧丽, 赵丹, 王丽娟, 周瑜, 曾丹林. 尿素对聚己内酯二醇结晶性能的影响研究[J]. 化工新型材料, 2018, 46(11): 173-176.
Wang Wanwan, Chen Hongxiang, Dai Qiaoli Zhao Dan, Wang Lijuan, Zhou Yu, Zeng Danlin. Influence of urea on crystallization of polycaprolactone. New Chemical Materials, 2018, 46(11): 173-176.
链接本文:  
http://www.hgxx.org/CN/  或          http://www.hgxx.org/CN/Y2018/V46/I11/173
[1] Coombes A G A,Rizzi S C,Williamson M,et al.Precipitation casting of polycaprolactone for applications in tissue engineering and drug delivery[J].Biomaterials,2004,25(2):315-325.
[2] PotrČT,Baumgartner S,Roškar R,et al.Electrospun polycaprolactone nanofibers as a potential oromucosal delivery system for poorly water-soluble drugs[J].Eur J Pharm Sci,2015,75:101-113.
[3] Karuppuswamy P,Venugopal J R,Navaneethan B,et al.Polycaprolactone nanofibers for the controlled release of tetracycline hydrochloride[J].Mater Lett,2015,141:180-186.
[4] Pilipchuk S P,Monje A,Jiao Y,et al.Integration of 3D printed and micropatterned polycaprolactone scaffolds for guidance of oriented collagenous tissue formation in vivo[J].Adv Healthc Mater,2016,5(6):676-687.
[5] Chen C H,Chen S H,Shalumon K T,et al.Prevention of peritendinous adhesions with electrospun polyethylene glycol/polycaprolactone nanofibrous membranes[J].Colloid Surface B,2015,133:221-230.
[6] Gao X,Song J,Zhang Y,et al.Bioinspired design of polycaprolactone composite nanofibers as artificial bone extracellular matrix for bone regeneration application[J].ACS Appl Mater Inter,2016,8(41):27594-27610.
[7] Lanfranconi M,Alvarez V A,Ludueña L N.Isothermal crystallization of polycaprolactone/modified clay biodegradable nanocomposites[J].J Therm Anal Calorim,2016,126(3):1273-1280.
[8] López J V,Pérez-Camargo R A,Zhang B,et al.The influence of small amounts of linear polycaprolactone chains on the crystallization of cyclic analogue molecules[J].RSC Adv,2016,6(53):48049-48063.
[9] Yilgör E,Isik M,Söz C K,et al.Synthesis and structure-property behavior of polycaprolactone-polydimethylsiloxane-polycaprolactone triblock copolymers[J].Polymer,2016,83:138-153.
[10] 乔从德,蒋世春,姬相玲,等.聚ε-己内酯薄膜的受限结晶行为研究[J].高分子学报,2006(8):964-969.
[11] Borsacchi S,Paderni K,Messori M,et al.Insights into shape-memory poly(ε-caprolactone) materials by solid-state NMR[J].Macromolecules,2014,47(11):3544-3552.
[12] Alvarado-Tenorio B,Romo-Uribe A,Mather P T.Microstructure and phase behavior of POSS/PCL shape memory nanocomposites[J].Macromolecules,2011,44(14):5682-5692.
[1] 李子庆, 赫文秀, 张永强, 于慧颖, 李兴盛, 刘斌. 不同温度对石墨烯掺氮位点的影响及性能测试[J]. 化工新型材料, 2018, 46(8): 174-178.
[2] 李姝靓, 赵春霞, 苟浩澜, 赖书琪, 黄浩然. 水溶性苯并噁嗪单体的合成及结晶性能分析[J]. 化工新型材料, 2018, 46(6): 199-201.
[3] 刘刚, 肖立华, 付超. 聚偏氟乙烯熔体结晶行为和高温极性相的产生[J]. 化工新型材料, 2018, 46(6): 165-167.
[4] 贺小平, 王唯赫, 李薇. 五角枫叶吸附结晶紫性能研究[J]. 化工新型材料, 2018, 46(6): 156-159.
[5] 卢月美, 杨孟进, 王世伟, 施企明, 刘建仁. CNTs/PPG/PP复合材料的非等温结晶行为[J]. 化工新型材料, 2018, 46(6): 144-147.
[6] 梅林玉, 成博, 刘峰, 王俊元. 磁场对电纺聚丙烯腈纤维聚集态结构和性能的影响[J]. 化工新型材料, 2018, 46(5): 103-106.
[7] 郑晗, 王新威, 孙勇飞, 张玉梅, 吴向阳. 超高分子量聚乙烯纤维结晶行为研究进展[J]. 化工新型材料, 2018, 46(5): 16-19.
[8] 郑真, 丁成立, 李惠萍, 付静静. 疏水性棉短绒纤维素/SiO2复合气凝胶的制备及性能研究[J]. 化工新型材料, 2018, 46(4): 230-233.
[9] 黄安荣, 韦良强, 孙静, 戚远慧, 董珈豪. 多壁碳纳米管含量对聚丙烯/多壁碳纳米管介电复合材料性能的影响研究[J]. 化工新型材料, 2018, 46(3): 58-61.
[10] 郭军, 黄劲松, 刘廷国,. 均相水稻秸秆接枝物的制备及性能研究[J]. 化工新型材料, 2018, 46(3): 248-252.
[11] 李荣哲, 刘昆林, 徐敏, 李学锋, 彭少贤, 赵西坡. 聚乳酸木塑复合材料增韧研究进展[J]. 化工新型材料, 2018, 46(2): 247-251.
[12] 李春静, 杨瑞霞, 马浩, 金慧娇, 石晓东, 马文静. CH3NH3PbI2Br光吸收层薄膜的制备[J]. 化工新型材料, 2018, 46(2): 155-159.
[13] 张显勇, 王忠, 付蕾, 贾仕奎. 成核剂的添加对可降解材料聚乳酸结晶性影响的研究进展[J]. 化工新型材料, 2018, 46(11): 230-233.
[14] 王启强,邵水源. 尿素/丙烯酸合成保墒剂在碱性土壤中的应用研究[J]. 化工新型材料, 2017, 45(9): 232-234.
[15] 周存,孙菲. 水溶液中磷酸二氢钾结晶影响因素的研究[J]. 化工新型材料, 2017, 45(9): 193-195.
No Suggested Reading articles found!
Viewed
Full text


Abstract

Cited

  Shared   
  Discussed   
京ICP备09035943号-38
版权所有 © 《化工新型材料》编辑部
本系统由北京玛格泰克科技发展有限公司设计开发 技术支持:support@magtech.com.cn