水热时间对纳米MoS2形貌 及光催化性能的控制研究
吴正颖1,毛安雯2,黄海1,盛备备2,刘劲松2*
1.苏州科技大学化学生物与材料工程学院,江苏省环境功能材料重点实验室,苏州215009;
2.南京航空航天大学材料科学与技术学院,南京211106
Influence of hydrothermal time on morphology and photocatalysis of MoS2 nanomaterial
Wu Zhengying1,Mao Anwen2,Huang Hai1,Sheng Beibei2,Liu Jinsong2
1.School of Chemistry Biology and Material Engineering,Jiangsu Key Laboratory for Environment Functional Materials,Suzhou University of Science and Technology, Suzhou 215009;
2.College of Material Science and Technology, Nanjing University of Aeronautics and Astronautics,Nanjing 211106
下载:  PDF (2881KB) 
输出:  BibTeX | EndNote (RIS)      
摘要 采用水热合成法制得二硫化钼(MoS2)粉末,详细研究了水热时间对产物形貌及光催化降解性能的影响。首先采用粉末X射线衍射仪(XRD)和场发射扫描电子显微镜(FE-SEM)对产物MoS2进行了表征,然后利用光催化技术评价了MoS2对模拟有机污染物亚甲基蓝的降解性能。结果表明:水热时间的延长有利于改善产物MoS2的形貌规整性,从而进一步提高其光催化性能,水热反应24h制得的MoS2在光照90min条件下,对亚甲基蓝(MB)的光降解率达到91.29%。
服务
把本文推荐给朋友
加入引用管理器
E-mail Alert
RSS
作者相关文章
吴正颖
毛安雯
黄海
盛备备
刘劲松
关键词:  MoS2粉末  水热法  光催化    
Abstract: Molybdenum disulfide (MoS2) powders were synthesized by hydrothermal method,and the effect of hydrothermal time on morphology and photocatalytic performance of MoS2 nanomaterials was studied.The MoS2 products were characterized by X-ray diffraction (XRD),and field emission scanning electron microscopy (FESEM).Photocatalytic performance of MoS2 powders for degradation of methylene blue was also measured by degrading methylene blue (MB).Results showed that the longer hydrothermal time was benefits for the more regular morphology of MoS2,resulting in the higher MB degradation efficiency.The MoS2 powders synthesized at 24h can degrade about 91.29% of MB within 90min under irradiation.
Key words:  MoS2 powder    hydrothermal method    photocatalytic performance
                    发布日期:  2018-11-06      期的出版日期:  2018-11-06
基金资助: 江苏省自然科学基金面上项目(BK20151198);南京航空航天大学材料科学与技术学院第四期创新基金创新项目(201606)
通讯作者:  刘劲松(1977-),男,博士,副教授,主要从事功能微纳米材料研究。   
作者简介:  吴正颖(1979-),女,博士,副教授,主要从事功能微纳米材料的合成、表征与性能研究。
引用本文:    
吴正颖,毛安雯,黄海,盛备备,刘劲松. 水热时间对纳米MoS2形貌 及光催化性能的控制研究[J]. 化工新型材料, 2018, 46(10): 204-206.
Wu Zhengying,Mao Anwen,Huang Hai,Sheng Beibei,Liu Jinsong. Influence of hydrothermal time on morphology and photocatalysis of MoS2 nanomaterial. New Chemical Materials, 2018, 46(10): 204-206.
链接本文:  
http://www.hgxx.org/CN/  或          http://www.hgxx.org/CN/Y2018/V46/I10/204
[1] Benavente E,Santa Ana M,Mendiz bal F,et al.Intercalation chemistry of molybdenum disulfide[J].Coordination Chemistry Reviews,2002,224(1):87-109.
[2] Frank S N,Bard A J.Heterogeneous photocatalytic oxidation of cyanide and sulfite in aqueous solutions at semiconductor powders[J].The Journal of Physical Chemistry,1977,81(15):1484-1488.
[3] Zhang Z J,Zhang J,Xue Q J.Synthesis and characterization of a molybdenum disulfide nanocluster[J].The Journal of Physical Chemistry,1994,98(49):12973-12977.
[4] Tenne R,Margulis L,Genut M,et al.Polyhedral and cylindrical structures of tungsten disulphide[J].Nature,1992,360(6403):444-446.
[5] Yu Y,Huang S Y,Li Y,et al.Layer-dependent electrocatalysis of MoS2 for hydrogen evolution[J].Nano Letters,2014,14(2):553-558.
[6] 王跃峰,赵鹏,曾一,等.化学气相沉积法制备富勒烯结构二硫化钼纳米粒子[J].应用化工,2008(12):1413-1415.
[7] Wu Z,Wang D,Sun A.Preparation of MoS2 nanoflakes by a novel mechanical activation method[J].Journal of Crystal Growth,2010,312(2):340-343.
[8] Deepak F L,Mayoral A,Yacaman M J.Faceted MoS2 nanotubes and nanoflowers[J].Materials Chemistry and Physics,2009,118(2):392-397.
[9] Wang H,Skeldon P,Thompson G,et al.Synthesis and characterization of molybdenum disulphide formed from ammonium tetrathiomolybdate[J].Journal of Materials Science,1997,32(2):497-502.
[10] Chhowalla M,Amaratunga G A.Thin films of fullerene-like MoS2 nanoparticles with ultra-low friction and wear[J].Nature,2000,407(6801):164-167.
[11] Sen R,Govindaraj A,Suenaga K,et al.Encapsulated and hollow closed-cage structures of WS2 and MoS2 prepared by laser ablation at 450~1050℃[J].Chemical Physics Letters,2001,340(3):242-248.
[12] 傅重源,邢淞,沈涛,等.水热法合成纳米花状二硫化钼及其微观结构表征[J].物理学报,2015,64(1):204-209.
[13] 宋也黎,李国伟,晋跃,等.水热法合成花状MoS2纳米粉及其摩擦学性能[J].机械工程材料,2011(6):49-52.
[14] Ye L,Guo W,Yang Y,et al.Directing the architecture of various MoS2 hierarchical hollow cages through the controllable synthesis of surfactant/molybdate composite precursors[J].Chemistry of Materials,2007,19(25):6331-6337.
[15] Vanchura B A,He P,Antochshuk V,et al.Direct synthesis of mesostructured lamellar molybdenum disulfides using a molten neutral n-alkylamine as the solvent and template[J].Journal of the American Chemical Society,2002,124(41):12090-12091.
[16] 曾颖峰,蒋晓明,陈月珠.表面活性剂对制备纳米MoS2颗粒的影响[J].石油学报(石油加工),2001,17(4):55-58.
[17] Sheng B B,Liu J S,Li Z Q,et al.Effects of excess sulfur source on the formation and photocatalytic properties of flower-like MoS2 spheres by hydrothermal synthesis[J].Materials Letters,2015,144:153-156.
[18] Tian Y,He Y,Zhu Y.Low temperature synthesis and characterization of molybdenum disulfide nanotubes and nanorods[J].Materials Chemistry and Physics,2004,87(1):87-90.
[1] 李文斌, 荆涛, 田景芝, 李艳云, 邓启刚. 可溶性淀粉/三维氮掺杂石墨烯电化学性能研究[J]. 化工新型材料, 2018, 46(9): 109-112.
[2] 丁世环, 徐聪聪, 鹿媛铮. SnS2/BiOBr复合光催化剂的制备及其光催化性能研究[J]. 化工新型材料, 2018, 46(9): 205-208.
[3] 刘雪佳, 张有为, 张丹丹, 郑冀. 水热法制备ZnO抗静电导电粉研究[J]. 化工新型材料, 2018, 46(9): 253-255.
[4] 张艳苹, 刘海峰, 霍冀川. 钙钛矿型氧化物薄膜的制备及光催化降解染料的研究进展[J]. 化工新型材料, 2018, 46(9): 55-59.
[5] 陈萍, 刘婷, 姚凯波, 袁国秋, 石磊, 葛存旺. 石墨烯量子点修饰TiO2复合纳米材料的制备及其光电性能研究[J]. 化工新型材料, 2018, 46(8): 79-84.
[6] 杨晓龙, 张义, 刘子森, 夏世斌, 贺锋, 吴振斌. 纳米光催化剂处理难降解性有机物的研究进展[J]. 化工新型材料, 2018, 46(8): 38-41.
[7] 蔡婷婷, 刘镕玮, 王媛媛, 翟永星, 段泽张建. 镍钴硫化物/碳微球电极的制备与电化学性能测试[J]. 化工新型材料, 2018, 46(8): 119-122.
[8] 熊乐艳, 张楠, 郭赞如, 马伟, 郑龙珍. 掺N纳米TiO2光催化材料的制备及其光催化性能研究[J]. 化工新型材料, 2018, 46(8): 97-101.
[9] 何登良, 张蓝心, 舒小元, 刘树信. 纳米ZnO/电气石复合粉体的制备及其对亚甲基蓝光催化性能的研究[J]. 化工新型材料, 2018, 46(8): 93-96.
[10] 黄云镜, 于计生, 唐丽梅, 李青松. 太阳光下TiO2光催化还原Cr(Ⅵ)影响因素研究[J]. 化工新型材料, 2018, 46(8): 191-194.
[11] 李杰, 逄显娟, 宋晨飞. 钒酸铋的选择性合成及其光催化性能研究[J]. 化工新型材料, 2018, 46(8): 217-220.
[12] 张慧莉. 一步法制备Fe2O3/碳纳米管复合材料及其电化学性能研究[J]. 化工新型材料, 2018, 46(7): 148-150.
[13] 李远勋, 李荡, 陈振玲. Ag、Cu掺杂TiO2催化剂的制备及其光催化降解阿昔洛韦的研究[J]. 化工新型材料, 2018, 46(7): 143-147.
[14] 龙森, 庹必阳, 谢飞, 韩朗, 徐科. 钛柱撑蒙脱石的制备及对亚甲基蓝的光催化降解研究[J]. 化工新型材料, 2018, 46(7): 198-201.
[15] 刘勇, 寇璐垚, 付孝锦, 由耀辉, 黄成华, 郑小刚. ZnFe2O4/g-C3N4对甲基橙的紫外光催化降解行为[J]. 化工新型材料, 2018, 46(7): 202-204.
No Suggested Reading articles found!
Viewed
Full text


Abstract

Cited

  Shared   
  Discussed   
版权所有 © 《化工新型材料》编辑部
本系统由北京玛格泰克科技发展有限公司设计开发 技术支持:support@magtech.com.cn