化工新型材料  2018, Vol. 46 Issue (10): 115-118    
  新材料与新技术 本期目录 | 过刊浏览 | 高级检索 |
PEG辅助溶剂热合成锂离子电池 纳米正极材料磷酸铁锂的研究
陈慧慧,王娟*,许云华
西安建筑科技大学机电工程学院陕西省纳米材料与技术重点实验室,西安710055
Study on polyethylene glycol-assisted solvothermal synthesis of lithium iron phosphate nanoparticle for lithium-ion battery
Chen Huihui, Wang Juan , Xu Yunhua
School of Mechanical and Electrical Engineering,Xi'an University of Architecture and Technology,Shaanxi Key Laboratory of Nano Materials and Technology,Xi'an 710055
下载:  PDF (1946KB) 
输出:  BibTeX | EndNote (RIS)      
摘要 在一元溶剂的基础上,以不同分子量的聚乙二醇(PEG)-水作为共溶剂,采用溶剂热法制备磷酸铁锂(LiFePO4),并制得锂离子电池纳米正极材料,并对产物的结构、形貌和电化学性能进行了研究。研究结果表明:溶剂PEG的引入具有对材料颗粒细化的作用,有效的减小锂离子的扩散和迁移途径,在PEG分子量为600制得的锂离子电池纳米正极材料的颗粒尺寸最小,在0.1C倍率条件下,放电比容量达147.1mAh/g,经过50次循环后容量保持率为92.5%,且电荷转移阻抗最小为125Ω。
服务
把本文推荐给朋友
加入引用管理器
E-mail Alert
RSS
作者相关文章
陈慧慧
王娟
许云华
关键词:  磷酸铁锂  溶剂热  共溶剂  纳米粒子  PEG    
Abstract: Based on the study of one dimension solvent,the nano-LiFePO4 for Li-ion battery anode was prepared via solvothermal method using polyethylene glycol (PEG) with different molecular weight in a water-polyethylene glycol (PEG) binary solvent.Research indicated:the introduction of solvent PEG had the effect of refining the material particles,effectively reducing the diffusion and migration pathway of Li ions.When PEG molecular weight was 600,the particle size was the smallest.At 0.1C rate,the specific discharge capacity was 147.1mAh/g.After 50 cycles,the capacity retention rate was 92.5%.Charge transfer resistance was 125Ω.
Key words:  lithium iron phosphate    solvothermal synthesis    co-solvent    nanoparticle    PEG
                    发布日期:  2018-11-06      期的出版日期:  2018-11-06
基金资助: 国家自然科学基金(51202179);教育部科学技术研究重点项目(212174);陕西省自然科学基金(2013KJXX-57);陕西省教育厅自然科学基金项目(14JS047,14JS048,16JS058);国家国际科技合作专项资助(2015DFR50350);金川-西安建筑科技大学预研究项目(X06071)
通讯作者:  王娟(1978-),女,教授,硕士研究生导师,研究方向为锂离子电池、太阳能电池材料、纳米材料。   
作者简介:  陈慧慧(1990-),女,硕士,从事锂离子电池正极材料的研究。
引用本文:    
陈慧慧,王娟,许云华. PEG辅助溶剂热合成锂离子电池 纳米正极材料磷酸铁锂的研究[J]. 化工新型材料, 2018, 46(10): 115-118.
Chen Huihui,Wang Juan,Xu Yunhua. Study on polyethylene glycol-assisted solvothermal synthesis of lithium iron phosphate nanoparticle for lithium-ion battery. New Chemical Materials, 2018, 46(10): 115-118.
链接本文:  
http://www.hgxx.org/CN/  或          http://www.hgxx.org/CN/Y2018/V46/I10/115
[1] Park O K,Cho Y,Lee S,et al.Who will drive electric vehicles,olivine or spinel[J].Energy & Environmental Science,2011,4(5):1621-1633.
[2] Bewlay S L,Konstantinov K,Wang G X,et al.Conductivity improvements to spray-produced LiFePO4 by addition of a carbon source[J].Materials Letters,2004,58:1788-1791.
[3] Srinivasan V,Newman J.Existence of path-dependence in the LiFePO4 electrode[J].Electrochemical and Solid-State Letters,2006,9(3):A110-A114.
[4] Gabersce K,Dominko R,Jamnik J.Is small particle size more important than carbon coating:an example study on LiFePO4 cathodes[J].Electrochem Soc,2007,9(12):2778-2783.
[5] Franger S,Benott C,Bouron C,et al.Chemistry and electro-chemistry of composite LiFePO4 materials for secondary lithium batteries[J].Phys Chem Solids,2006,67(5/6):1338-1342.
[6] Kim C W,Park J S,Lee K S.Effect of Fe2P on the electron conductivity and electrochemical performance of LiFePO4 synthesized by mechanical alloying using Fe3+ raw material[J].J Power Sources,2006,163(1):144-150.
[7] Zhou N,Wang H Y,Uchaker E,et al.Additive-free solvothermal synthesis and Li-ion intercalation properties of dumbbell-shaped LiFePO4/C mesocrystals[J].Journal of Power Sources,2013,239(10):103-110.
[8] Konarova M,Taniguchi I.Preparation of carbon coated LiFePO4 by a combination of spray pyrolysis with planetary ball-milling followed by heat treatment and their electrochemical properties[J].Powder Technology,2009,191(1/2):111-116.
[9] Bhattacharyya S,Gedanken A.Microwave-assisted insertion of silver nanoparticles into 3-D mesoporous zinc oxide nanocomposites and nanorods[J].J Phys Chem C,2008,112(3):659-665.
[10] 尚怀芳.锂离子电池正极材料LiFePO4和LiMn2O4的表面结构及电化学性性能研究[D].北京:北京工业大学,2013.
[11] Sun C,Rajasekhara S,Goodenough J B,et al.Monodisperse porous LiFePO4 microspheres for a high power Li-ion battery cathode[J].Journal of the American Chemical Society,2011,133(7):2132-2135.
[12] Ghafarian-Zahmatkesh H,Javanbakht M,Ghaemi M.Ethylene glycol-assisted hydrothermal synthesis and characterization of bow-tie-like lithium iron phosphate nanocrystals for lithium-ion batteries[J].Journal of Power Sources,2015,284(1):339-348.
[13] Tajimi S,Ikeda Y,Uematsu K,et al.Enhanced electrochemical performance of LiFePO4 prepared by hydrothermal reaction[J].Solid State Ionics,2004,175(1/4):287-290.
[14] 程菲,孙蔷,陆安慧,等.溶剂热法制备锂离子电池正极材料磷酸铁锂[J].电源技术,2013,37(5):744-746.
[15] Ni J,Morishita M,Kawabe Y,et al.Hydrothermal preparation of LiFePO4 nanocrystals mediated by organic acid[J].J Power Sources,2010,195(9):2877-2882.
[1] 张有为, 马慧玲, 刘平桂, 赫丽华, 罗文, 单明正. 石墨烯-镍纳米复合材料的辐射制备及其电磁行为研究[J]. 化工新型材料, 2018, 46(9): 101-104.
[2] 贾济如, 王潮霞, 殷允杰. 静电纺丝法制备吲哚美辛纳米粒子/聚乙烯醇复合纤维膜[J]. 化工新型材料, 2018, 46(9): 88-90.
[3] 武宏大, 杨占旭, 邵军桥. 溶剂热法制备球形MoS2材料及其电化学性能研究[J]. 化工新型材料, 2018, 46(9): 180-182.
[4] 董淑玲, 翁婷, 王秀玲, 王红霞, 刘勇健. 磁性荧光双功能纳米材料Fe3O4/CS@CQDs的制备与表征[J]. 化工新型材料, 2018, 46(9): 121-124.
[5] 熊乐艳, 张楠, 郭赞如, 马伟, 郑龙珍. 掺N纳米TiO2光催化材料的制备及其光催化性能研究[J]. 化工新型材料, 2018, 46(8): 97-101.
[6] 张敏, 王晓, 孙红梅, 拜科·诺夫, 杨超, 宿新泰. Ni/Al2O3/C的合成及催化CO甲烷化反应性能研究[J]. 化工新型材料, 2018, 46(7): 191-193.
[7] 李春雷, 解莹春, 李祥飞. 磷酸铁锂正极材料的制备及改性研究进展[J]. 化工新型材料, 2018, 46(7): 25-28.
[8] 刘勇智, 陈国力, 王雅珍, 殷广明. 改性纳米粒子及高分子吸附材料的研究进展[J]. 化工新型材料, 2018, 46(7): 14-17.
[9] 朱冠南, 李宁, 程小雨, 赵靓, 王海涛, 税粒珂, 李坚, 汪称意, 任强. 聚甲基丙烯酸N,N-二甲胺基乙酯-b-聚甲基丙烯酸十二氟庚酯嵌段共聚物的合成及其在疏水涂层的应用[J]. 化工新型材料, 2018, 46(5): 238-241.
[10] 李林, 刘振新, 徐蓓, 李晶晶, 吴德鹏, 李鸿阳, 张晓, 姚纪伟, 邵晨, 贾巧娟, 方少明, 王力臻, 邢宇. 节省锂资源的磷酸铁锂水热合成路径[J]. 化工新型材料, 2018, 46(3): 187-189.
[11] 翁婷, 王胜男, 王秀玲, 董淑玲, 刘勇健. 碳量子点磁性纳米复合材料的制备与表征[J]. 化工新型材料, 2018, 46(2): 222-225.
[12] 齐美洲, 汪志全, 李道聪, 杨茂萍. LiMn1-xFexPO4正极材料制备方法的研究进展[J]. 化工新型材料, 2018, 46(2): 59-62.
[13] 曾月, 付珍珍, 李增威, 王娜, 雷婵, 陈姝娟. 磁性纳米分子印迹聚合物的制备及其在食品安全检测中的应用研究[J]. 化工新型材料, 2018, 46(1): 1-4.
[14] 鲁文凡, 吕帅帅, 李志扬, 汪兴兴, 倪红军. 电动汽车用磷酸铁锂动力电池内阻特性研究[J]. 化工新型材料, 2018, 46(1): 175-177.
[15] 梁健, 杨飞, 张永明, 范例. 溶剂热法制备α-V2O5空心纳米微球及其电化学性能研究[J]. 化工新型材料, 2017, 45(9): 121-123.
No Suggested Reading articles found!
Viewed
Full text


Abstract

Cited

  Shared   
  Discussed   
版权所有 © 《化工新型材料》编辑部
本系统由北京玛格泰克科技发展有限公司设计开发 技术支持:support@magtech.com.cn