化工新型材料  2018, Vol. 46 Issue (9): 140-143    
  科学研究 本期目录 | 过刊浏览 | 高级检索 |
基于静电纺-层层组装技术制备[壳聚糖/海藻酸钠]c/l/聚乙烯醇纳米复合膜
王其智1,2, 汪滨1,2, 王娇娜1,2*, 漆麟1,2, 李从举1,2
1.北京服装学院材料科学与工程学院,北京市服装材料研究开发与评价重点实验室,北京100029;
2.北京市纺织纳米纤维工程技术研究中心,北京100029
Preparation of [CTS/SA]c/lPVA nanocomposite film based on electrospinning and layer-by-layer assembly
Wang Qizhi1,2, Wang Bin1,2, Wang Jiaona1,2, Qi Lin1,2, Li Congju1,2
1.College of Material Science and Engineering,Beijing Institute of Fashion Technology,Beijing Key Laboratory of Clothing Materials R&D and Assessment,Beijing 100029;
2.Beijing Engineering Research Center of Textile Nanofiber,Beijing Institute of Fashion Technology,Beijing 100029
下载:  PDF (3630KB) 
输出:  BibTeX | EndNote (RIS)      
摘要 静电纺丝技术在近几十年来得到了快速发展,静电纺丝制备的纳米纤维具有比表面积大和孔隙率高的优点,因而广泛应用于海水淡化、电池隔膜和重金属离子吸附等领域。结合层层组装法,以交联的静电纺聚乙烯醇(PVA)为基底,壳聚糖(CTS)和海藻酸钠(SA)为聚电解质,成功制备了复合纳米纤维膜,并对复合膜表面的聚电解质层(PEL)进行了交联,考察复合膜的抗水解性能。结果表明:交联最佳条件为戊二醛/丙酮=2.0%(质量分数)、时间3h、pH=2。
服务
把本文推荐给朋友
加入引用管理器
E-mail Alert
RSS
作者相关文章
王其智
汪滨
王娇娜
漆麟
李从举
关键词:  静电纺丝  纳米纤维  层层组装  复合膜交联    
Abstract: The electrospun technology has developed rapidly in recent decade years.Since the nanofibers have high porosity and a large specific surface area,which is widely used in the fields of desalination,battery separators,air filtration and adsorption of heavy metal ions.Combined with layer-by-layer assembly (LbL) method,the composite nanofiber membranes were successfully prepared by using cross-linked electrospinning PVA as the substrate,CTS and SA as the polyelectrolyte.And PEL layer on the surface of membrane was cross-linked.The optimum conditions of cross-linking were GA50%/acetone=2.0wt%,3h,pH=2.
Key words:  electrospin    nanofiber    layer-by-layer assembly    composite membrane cross-linking
收稿日期:  2017-04-24                     发布日期:  2018-11-05      期的出版日期:  2018-09-20
基金资助: 国家自然科学基金(51503005、21274006);北京市自然科学基金(2182014);北京市科协“金桥工程种子资金”(H2017-42);北京市教育委员会科技计划一般项目(SQKM201710012004);北京服装学院高水平教师队伍建设专项资金(BIFTQG201801);北京市科技北京百名领军人才工程(Z161100004916168);北京市优秀人才(2017000020124G089)
通讯作者:  王娇娜(1985-),女,讲师,主要研究方向为纳米技术与纤维材料。   
作者简介:  王其智(1992-),男,硕士研究生,主要研究方向为纳米纤维材料。
引用本文:    
王其智, 汪滨, 王娇娜, 漆麟, 李从举. 基于静电纺-层层组装技术制备[壳聚糖/海藻酸钠]c/l/聚乙烯醇纳米复合膜[J]. 化工新型材料, 2018, 46(9): 140-143.
Wang Qizhi, Wang Bin, Wang Jiaona, Qi Lin, Li Congju. Preparation of [CTS/SA]c/lPVA nanocomposite film based on electrospinning and layer-by-layer assembly. New Chemical Materials, 2018, 46(9): 140-143.
链接本文:  
http://www.hgxx.org/CN/  或          http://www.hgxx.org/CN/Y2018/V46/I9/140
[1]刘力菲,李伟,黄潇楠.静电纺丝纳米纤维的制备与应用[J].首都师范大学学报(自然科学版),2017,38(1):58-63.
[2]Ahmed F E,Lalia B S,Hashaikeh R.A review on electrospinning for membrane fabrication:challenges and applications[J].Desalination,2015,356:15-30.
[3]Tijing L D,Choi J S,Lee S,et al.Recent progress of membrane distillation using electrospun nanofibrous membrane[J].Journal of Membrane Science,2014,453:435-462.
[4]Richardson J J,Bjornmalm M,Caruso F.Multilayer assembly technology-driven layer-by-layer assembly of nanofilms[J].Science,2015,348(6233):2491.
[5]Xu G R,Wang S H,Zhao H L,et al.Layer-by-layer (LBL) assembly technology as promising strategy for tailoring pressure-driven desalination membranes[J].Journal of Membrane Science,2015,493:428-443.
[6]何东保,毅石,梁红波,等.壳聚糖-海藻酸钠协同相互作用及其凝胶化的研究[J].武汉大学学报理学版,2002,48(2):193-196.
[7]张鸿鑫,鲁路,李立华,等.海藻酸动态共价交联水凝胶的制备及其自愈合性能[J].高分子学报,2016(3):368-374.
[8]韩雪,曹蒋永荃,周江玲,等.基于壳聚糖的pH响应双重药物释放系统研究[J].高分子学报,2015(12):1471-1476.
[9]刘燕君,王娇娜,李从举.基于静电纺丝技术的PET/PVA复合超滤膜制备条件的探索[J].高分子学报,2013(9):1137-1142.
[10]Zhang M,Wang J,Li C.Low pressure-driven thin film composite membranes for Cr(Ⅵ) removal based on nanofibrous mats supported layer-by-layer assembly coatings[J].Polymer Engineering & Science,2014,55(2):421-428.
[11]Ma H,Burger C,Hsiao B S,et al.Ultrafine polysaccharide nanofibrous membranes for water purification[J].Biomacromolecules,2011,12(4):970-976.
[1] 程金生, 钟瑞敏, 万维宏, 朱建华, 陈信炎. 谷壳源胺基修饰的石墨烯纳米纤维对水样中酸性大红GR脱除性能研究[J]. 化工新型材料, 2018, 46(9): 113-116.
[2] 张金宁, 宋明玉, 陈昀, 曹建华, 杨占平, 徐阳, 魏取福. 二醋酸/有机改性蒙脱土复合多孔纤维的制备及其染料吸附性能[J]. 化工新型材料, 2018, 46(9): 144-147.
[3] 贾济如, 王潮霞, 殷允杰. 静电纺丝法制备吲哚美辛纳米粒子/聚乙烯醇复合纤维膜[J]. 化工新型材料, 2018, 46(9): 88-90.
[4] 张艺萌, 彭程程, 张权, 徐阳, 王清清. PVA-SbQ/透明质酸复合纳米纤维的制备及表征[J]. 化工新型材料, 2018, 46(8): 231-233.
[5] 孟亚飞, 裴广玲. 静电纺纳米纤维膜处理重金属离子污水研究进展[J]. 化工新型材料, 2018, 46(8): 281-284.
[6] 刘玥波, 王娇娜, 汪滨, 李从举. 静电纺PA56纳米纤维膜的制备及力学性能研究[J]. 化工新型材料, 2018, 46(8): 149-152.
[7] 王循, 丁玉梅, 李好义, 谭晶, 杨卫民, 阎华. 聚合物电纺纳米纤维高效油污染处理应用研究进展[J]. 化工新型材料, 2018, 46(7): 48-51.
[8] 魏安方, 王娟, 魏取福, 凤权. 纳米羟基磷灰石/聚乳酸复合纳米纤维支架材料的研究[J]. 化工新型材料, 2018, 46(6): 78-81.
[9] 王茜, 李亚婷, 郭巧静, 赵彦生, 陈小玲. 聚天冬氨酸/壳聚糖季铵盐层层组装膜负载缓释两种正电荷药物的研究[J]. 化工新型材料, 2018, 46(6): 171-175.
[10] 戴剑锋, 闫兴山, 田西光, 李维学, 王青. 静电纺丝法制备尖晶石型LiMn2O4纳米纤维锂离子电池正极材料[J]. 化工新型材料, 2018, 46(5): 204-207.
[11] 赵树宇, 王娇娜, 汪滨, 李从举. NaA型分子筛掺杂PAN/PES复合纳米纤维膜制备及性能研究[J]. 化工新型材料, 2018, 46(5): 67-70.
[12] 张金宁, 宋明玉, 陈昀, 曹建华, 杨占平, 徐阳, 魏取福. 静电纺多孔/无孔二醋纤复合膜的制备及过滤性能研究[J]. 化工新型材料, 2018, 46(5): 52-55.
[13] 梅林玉, 成博, 刘峰, 王俊元. 磁场对电纺聚丙烯腈纤维聚集态结构和性能的影响[J]. 化工新型材料, 2018, 46(5): 103-106.
[14] 董峰, 魏占锋, 马舒慧, 黄帅超. 载银纳米纤维素-壳聚糖复合膜的表征及性能研究[J]. 化工新型材料, 2018, 46(5): 126-129.
[15] 马小彪, 陈思浩, 黎朝晖, 胡林. 三维Fe2O3/BC-CNFs复合负极材料的电化学性能研究[J]. 化工新型材料, 2018, 46(4): 131-134.
No Suggested Reading articles found!
Viewed
Full text


Abstract

Cited

  Shared   
  Discussed   
京ICP备09035943号-38
版权所有 © 《化工新型材料》编辑部
本系统由北京玛格泰克科技发展有限公司设计开发 技术支持:support@magtech.com.cn