Abstract: Carbamide was used as the source of N and tetrabutyl titanate as the source of Ti,by the sol-gel method to prepare N-TiO2,and it was characterized by scanning electron microscope (SEM),infrared Spectroscopy (IR),X-ray diffraction (XRD),X-ray photoelectron spectroscopy (XPS) and fluorescence spectra.The results showed that the size of N-TiO2 was about 20nm.Photoelectric ability of the composite was greatly reduced compared with the pure TiO2.4N-TiO2-500 as the most suitable photocatalyst,the photodegradation of Rhodamine 6G was simulated.The experiment indicated that the sample had a great ability of photocatalytic degradation.After irradiated by 500W high pressure mercury lamp,the degradation rate reached to 99.24%.By studying the catalyst durability,it was found that the rate of photocatalytic degradation of prepared material was up to 85.79% after 6 cycles.
[1] ORegan B,Grätzel M.A low-cost,high-efficiency solar cell based on dye-sensitized colloidal TiO2 films[J].Nature,1991,353(6346):737-740. [2] Hoffmann M R,Martin S T,Choi W Y,et al.Elemental applications of semiconductor photocatalysis[J].Chemical Reviews,1995,95(1):69-96. [3] Serpone N,Lawless D,Disdier J,et al.Spectroscopic,photoconductivity,and photocatalytic studies of TiO2 colloids:naked and with the lattice doped with Cr3+,Fe3+,and V5+ cations[J].Langmuir,1994,10(3):643-652. [4] S K,Raftery D.Visible light driven V-doped TiO2 photocatalyst and its photooxidation of ethanol[J].Journal of Physical Chemistry B,2001,105(14):2815-2819. [5] Asahi R,Morikawa T,Ohwaki T,et al.Visible-light photocatalysis in nitrogen-doped titanium oxides[J].Science,2001,293(5528):269. [6] Hiroshi I,Yuka W,Kazuhito H.Carbon-doped anatase TiO2 powders as a visible-light sensitive photocatalyst[J].Chemistry Letters,2003,32(8):772-773. [7] Umebayashi T,Yamaki T,Tanaka S,et al.Visible-light-induced degradation of methylene blue on S-doped TiO2[J].Chemistry Letters,2003,32(4):330-331. [8] Hong Xiaoting,Wang Zhengpeng,Cai Weimin,et al.Visible-light-activated nanoparticle photocatalyst of iodine-doped titanium dioxide[J].Chemistry of Materials,2005,17(6):1548-1552. [9] Wu P Y,Jiang Y P,Zhang Q Y,et al.Comparative study on arsenate removal mechanism of MgO and MgO/TiO2 composites:FT-IR and XPS analysis[J].New Journal of Chemistry,2016,40(3):2878-2885. [10] 黄涛,张国亮,王玲,等.以尿素为氮源制备氮改性二氧化钛及其改性机理[J].催化学报,2011,32(3):508-512. [11] Chen Y,Dionysiou D D.Bimodal mesoporous TiO2-P25 composite thick films with high photocatalytic activity and improved structural integrity[J].Applied Catalysis B Environmental,2008,80(1):147-155. [12] Wist J,Sanabria J,Dierolf C,et al.Evaluation of photocatalytic disinfection of crude water for drinking-water production[J].Journal of Photochemistry & Photobiology A Chemistry,2002,147(3):241-246. [13] Peng T,Zhao D,Dai K,et al.Synthesis of titanium dioxide nanoparticles with mesoporous anatase wall and high photocatalytic activity[J].Journal of Physical Chemistry B,2005,109(11):4947-4952. [14] 张青红.纳米氧化钛光催化材料及应用[M].北京:化学工业出版社材料科学与工程出版中心,2002.