Abstract: Two kinds of triblock copolymer diols of poly L-lactate (PLLA) and polyethylene glycol (PEG) were synthesized by ring-opening polymerization.The copolymers were end-capped with methacrylate to form macro-crosslinker poly (L-lactide)-b-polyethylene glycol-b-poly (L-lactide) dimethacrylates (PELAMA) for preparation of pH-responsive hydrogel poly (PLEAMA-Acrylic acid-N-isopropylacrylamide) (PELAMA-AN) through photo-polymerization using N-isopropylmethacylamide (NIPAM),acrylic acid (AA) as monomers.PELAMA was characterized with FT-IR and 1H-NMR.The swelling ratio of hydrogels in PBS at various pH values was studied.Simultaneously degradation property and the controlled drug release behavior of hydrogels were also investigated.The results showed that PELAMA-ANs were typical pH-responsive hydrogels.The swelling ratio (1000%~2000%) of hydrogels in pH=7.4 PBS was two times bigger than that in acidic environment (pH=1.2)(400%~500%).Meanwhile,the periodically swelling/diswelling property of the hydrogels was observed by switching the pH values.It was found that the release rate of the doxorubicin hydrochloride at acidic condition (20%~40%) was smaller than that in a neutral environment (50%~60%) with in 10h.Also,the hydrogel released drug killed HeLa cells,which indicated that the PELAMA-AN hydrogels had the potential to be used as anticancer drug carriers.
徐亮, 赵景, 陈泽旭, 李松彦, 盛扬, 孙一新, 张嵘. 以聚乳酸-b-聚乙二醇-b-聚乳酸二丙烯酸酯为交联剂的pH响应型水凝胶的制备及药物控制释放研究[J]. 化工新型材料, 2018, 46(3): 210-214.
Xu Liang, Zhao Jing, Chen Zexu, Li Songyan, Sheng Yang, Sun Yixin, Zhang Rong. Preparation of pH-responsive hydrogel based on triblock copolymer of polyL-lactate and polyethylene glycol for controlled drug release. New Chemical Materials, 2018, 46(3): 210-214.
[1] 高青雨,张玉娟,俞贤达.温度及pH敏感性N-乙烯基吡咯烷酮与丙烯酸β-羟基丙酯共聚物/聚(丙烯酸)互穿网络水凝胶的合成及其性能研究[J].高分子学报,2001(3):329-332. [2] Jiang B,Li B.Tunable drug loading and release from polypeptide multilayer nanofilms[J].Int J Nanomedicine,2009,4(1):37-53. [3] Medina S H,Chevliakov M V,Tiruchinapally G,et al.Enzyme-activated nanoconjugates for tunable release of doxorubicin in hepatic cancer cells[J].Biomaterials,2013,34(19):4655-4666. [4] 邓超,王荣,陈维,等.具生物活性的快速光交联生物可降解水凝胶的设计合成[J].高分子学报,2013(5):695-704. [5] Hu X,Wang Y,Zhang L,et al.Redox/pH dual stimuli-responsive degradable Salecan-g-SS-poly(IA-co-HEMA) hydrogel for release of doxorubicin[J].Carbohydrate Polymers,2017,155:242-251. [6] Pan Y J,Chen Y Y,Wang D R,et al.Redox/pH dual stimuli-responsive biodegradable nanohydrogels with varying responses to dithiothreitol and glutathione for controlled drug release[J].Biomaterials,2012,33(27):6570-6579. [7] Hiemstra C,Zhou W,Zhong Z,et al.Rapidly in situ forming biodegradable robust hydrogels by combining stereocomplexation and photopolymerization[J].Journal of the American Chemical Society,2007,129(32):9918-9926. [8] 冯学鹏,简鹏,丁琳,等.基于聚丙交酯的光固化型可生物降解聚氨酯丙烯酸酯的合成和表征[J].高分子学报,2016(7):949-958.