Abstract: Nickel cobalt sulfide was prepared by hydrothermal synthesis with different Ni/CO ratios of reactants.The products were characterized by X ray diffractometer and scanning electron microscope.The measurable electrode was prepared by using the prepared product as the active substance,the carbon microsphere as the conductive agent and the nickel foam as the matrix.The electrochemical properties of different electrodes were tested by cyclic voltammetry and constant current charge discharge.The electrode CV curve with a nickel content of 50% in the reactants showed a larger redox current density and the highest specific capacitance of 938.7F/g.
蔡婷婷, 刘镕玮, 王媛媛, 翟永星, 段泽张建. 镍钴硫化物/碳微球电极的制备与电化学性能测试[J]. 化工新型材料, 2018, 46(8): 119-122.
Cai Tingting, Liu Rongwei, Wang Yuanyuan, Zhai Yongxing, Duan Ze, Zhang Jian. Preparation and electrochemical performance test of nickel cobalt sulfide/carbon microsphere electrode. New Chemical Materials, 2018, 46(8): 119-122.
[1] Wu T H,Li X Y,Li L.Research review of composite electrode materials for super capacitor[J].Applied Mechanics and Materials,2016,4278(851):13-16. [2] 焦琛,张卫珂,苏方远,等.超级电容器电极材料与电解液的研究进展[J].新型炭材料,2017,32(2):106-115. [3] 万厚钊,缪灵,徐葵,等.MnO2基超级电容器电极材料[J].化工学报,2013,64(3):801-813. [4] Bonu V,Gupta B,Chandra S,et al.Electrochemical supercapacitor performance of SnO2 quantum dots[J].Electrochimica Acta,2016,203:230-237. [5] 肖富强,袁大庆,朱升云,等.超级电容器用镍钴硫化物电极材料的研究进展[J].功能材料,2017,48(9):9001-9006. [6] 叶星柯,周乾隆,万中全,等.柔性超级电容器电极材料与器件研究进展[J].化学通报,2017,80(1):10-33,76. [7] 朱红艳,赵建国,庞明俊,等.石墨烯/δ-MnO2复合材料的制备及其超级电容器性能[J].化工学报,2017,68(12):4824-4832. [8] Ajay K M,Dinesh M N.Influence of various activated carbon based electrode materials in the performance of super capacitor[J].IOP Conference Series:Materials Science and Engineering,2018,310(1):1-8. [9] Jamil A,Mustafa F,Aslam S,et al.Structural and optical properties of thermally reduced graphene oxide for energy devices[J].Chinese Physics B,2017,26(8):346-352. [10] 李雪芹,常琳,赵慎龙,等.基于碳材料的超级电容器电极材料的研究[J].物理化学学报,2017,33(1):130-148. [11] 于美,李新杰,马玉骁,等.石墨烯基复合超级电容器材料研究进展[J].材料工程,2016,44(5):101-111. [12] 孙刚伟.碳基超级电容器正负极不对称电容行为研究[D].上海:华东理工大学,2012. [13] 尤春琴,罗民,阚夏梅,等.皱褶表面介孔镍钴硫化物微球的制备及其超电性能[J].应用化学,2015,32(12):1455-1461. [14] 高阳,多元金属硫化物电极材料的制备及其超级电容器性能的研究[D].郑州:郑州大学,2015. [15] 余大江,多元镍钴化合物电极材料的制备及其电化学储能研究[D].杭州:浙江理工大学,2015. [16] 纪莹.锰/钴/镍基硫族化合物的合成及其电化学性质的研究[D].长春:吉林大学,2015. [17] 廖明佳,乔雷,陈海岸,等.镍钴硫化物的制备及其反应温度对形貌和超级电容器性能的影响[J].重庆大学学报,2016,39(6):95-100. [18] Li Guilin,Xu Cailing.Hydrothermal synthesis of 3D NixCo1-xS2 particles/graphene composite hydrogels for high performance supercapacitors[J].Carbon,2015,90(3):44-52. [19] Zhu Yirong,Wu Zhibin,Jing Mingjun,et al.Mesoporous NiCo2S4 nanoparticles as high-performance electrode materials for supercapacitors[J].Journal of Power Sources,2015,273:584-590. [20] 蔡婷婷,张梦莹,刘镕玮,等.碳微球的水热法制备与表征[J].信息记录材料,2017,18(8):49-50.