红色稀土荧光材料的制备及其在喷墨打印领域的应用研究
汤森进, 周剑, 邹文*
江西省核工业地质局测试研究中心,南昌330096
Preparation of red rare earth fluorescent material and its application in inkjet printing
Tang Senjin, Zhou Jian, Zou Wen
Testing Center of Jiangxi Nuclear Industry Geological Bureau,Nanchang 330096
下载:  PDF (1669KB) 
输出:  BibTeX | EndNote (RIS)      
摘要 对红色稀土荧光材料的制备及应用进行了研究。发现荧光材料的相对荧光亮度和产率受掺杂浓度、搅拌速率、pH和反应温度的影响。当掺杂浓度为n(Eu3+)∶n(Tb3+)=10∶1(质量比),搅拌速率为240r/min,pH=7,反应温度为35℃时,红色稀土荧光材料的产率较高,相对荧光亮度最好。此外,还提供了一种红色纳米荧光打印墨水的制备方法及主要物化性能参数,并展示了其打印后的效果。
服务
把本文推荐给朋友
加入引用管理器
E-mail Alert
RSS
作者相关文章
汤森进
周剑
邹文
关键词:  荧光材料  稀土  荧光打印墨水    
Abstract: The preparation and application of red rare earth fluorescent material were studied.It is found that the relative fluorescence intensity and yield of material were affected by the doping concentration,stirring rate,pH and reaction temperature.The yield was relatively high and relative fluorescence intensity was best when n(Eu3+)∶n(Tb3+)=10∶1,stirring speed was 240r/min,pH=7,reaction temperature was 35℃.In addition,it was also provided that a preparation method and the main physical and chemical performance parameters of a red nanometer fluorescent printing ink,and showed its effect when the ink was printed.
Key words:  fluorescent material    rare earth    fluorescent printing ink
收稿日期:  2016-11-09                出版日期:  2018-03-20      发布日期:  2018-04-09      期的出版日期:  2018-03-20
通讯作者:  邹文。   
作者简介:  汤森进(1966-),男,高级工程师,主要从事表面处理材料及精细化学品研究。
引用本文:    
汤森进, 周剑, 邹文. 红色稀土荧光材料的制备及其在喷墨打印领域的应用研究[J]. 化工新型材料, 2018, 46(3): 228-231.
Tang Senjin, Zhou Jian, Zou Wen. Preparation of red rare earth fluorescent material and its application in inkjet printing. New Chemical Materials, 2018, 46(3): 228-231.
链接本文:  
http://www.hgxx.org/CN/  或          http://www.hgxx.org/CN/Y2018/V46/I3/228
[1] 裴娟.光致发光稀土(铕、铽)配合物的合成、荧光性能及理论研究[D].天津:南开大学,2006.
[2] 杜洪.一种发黄光的铽配合物的合成、表征及其发光机理的初步探讨[D].太原:太原理工大学,2008.
[3] 赵永霞,聂志文,石孟孟,等.Y2O3∶Eu空心球的合成及其发光性能研究[J].江西师范大学学报:自然科学版,2015,39(4):415-419.
[4] 张美丽,王敏.稀土配合物[Pr(1,3-pda)0.5(nbca)2(H2O)2]的合成及结构研究[J].江西师范大学学报:自然科学版,2013,37(6):599-602.
[5] 王正祥,陈洪,舒万艮,等.紫外光固化掺Eu0.6Gd0.4(TTA)3phen水性荧光防伪油墨的制备与性能[J].稀有金属,2004,28(1):210-213.
[6] 张曦倩.铕三元配合物及红色荧光油墨树脂的制备及性能研究[D].长沙:湖南大学,2006.
[7] 梁波.铕配合物红色电致发光材料的合成及其电致发光器件的研究[D].湘潭:湘潭大学,2003.
[8] Rocha G B,Alves S,Brito H F,et al.Emission quantum yield of europium(Ⅲ) mixed complexes with thenoyltrifluoroacetonate and some aromatic ligands[J].Journal of Alloys & Compounds,2000,303-304:364-370.
[9] Gong M L,An B L,Cheah K W.Synthesis and bright luminescence of lanthanide (Eu(Ⅲ),Tb(Ⅲ)) complexes sensitized with a novel organic ligand[J].Chemical Physics Letters,2004,385(5):345-350.
[10] Nakamura K,Hasegawa Y,Wada Y,et al.Novel luminescent Eu(Ⅲ) complex with remarkably narrow emission band[J].Chemical Physics Letters,2004,398(4):500-504.
[11] Kim D,Jeong S,Lee S,et al.Organic thin film transistor using silver electrodes by the ink-jet printing technology[J].Thin Solid Films,2007,515(19):7692-7696.
[12] 刘其红.喷墨印刷技术原理与应用[J].印刷工业,2009,12(4):43-45.
[13] 卜广玖,王潮霞.二元醇对分散荧光染料墨水性能的影响[J].精细化工,2011,28(5):505-509.
[14] Zhang W,Wei X F,Huang B Q,et al.Study on the luminescent property of fluorescent inkjet ink based on additive color imaging[J].Applied Mechanics & Materials,2013,469(11):55-58.
[15] Tekin E,Holder E,Marin V,et al.Ink-jet printing of luminescent ruthenium- and iridium-containing polymers for applications in light-emitting devices[J].Macromolecular Rapid Communications,2005,26(26):293-297.
[1] 刘欢, 叶俊, 张弛. 新型二吡咯类有机荧光材料的合成及其性能研究[J]. 化工新型材料, 2018, 46(8): 244-246.
[2] 仝瑞, 吴婷, 廖丽雯, 赵士龙. Eu3+单掺和Er3+/Yb3+共掺Ba3Lu4O9的发光性能研究[J]. 化工新型材料, 2018, 46(5): 87-90.
[3] 邱治文, 孙晓刚, 庞志鹏, 刘珍红, 陈珑, 蔡满园. 稀土氧化物和碳纳米管共掺导电纸的电磁屏蔽性能研究[J]. 化工新型材料, 2018, 46(3): 75-79.
[4] 刘卫华, 罗军, 安晓龙, 葛明桥. 合成革的夜光整理及其性能研究[J]. 化工新型材料, 2018, 46(1): 240-243.
[5] 朱晓东, 王尘茜, 雷佳浩, 文桂岚, 易倩, 冯威. 稀土元素掺杂TiO2研究进展[J]. 化工新型材料, 2018, 46(1): 13-16.
No Suggested Reading articles found!
Viewed
Full text


Abstract

Cited

  Shared   
  Discussed   
版权所有 © 《化工新型材料》编辑部
本系统由北京玛格泰克科技发展有限公司设计开发 技术支持:support@magtech.com.cn